摘  要：本文详述了以凹凸棒土为原料，并加入氧化铝为骨料的凹土基分离膜的制备过程。制备过程中，通过控制氧化铝、羧甲基纤维素的含量，制胚压力、保温时间、烧结温度进行正交试验。简单介绍了制备支撑体的清洗和保存方法。检测了其接触角、抗压强度和纯水通量的值，分析了氧化铝含量及其他因素对膜支撑体性能的影响。94165

毕业论文关 键 词：膜支撑体, 凹凸棒土, 氧化铝, 抗压强度

Abstract：In this paper, the preparation process of attapulgite separation membrane with attapulgite as raw material and adding alumina as aggregate is described in detail。 In the preparation process, the orthogonal test was carried out by controlling the content of alumina, carboxymethyl cellulose, embryo pressure, holding time and sintering temperature。 The preparation and maintenance of the preparation of the support is briefly described。 The effects of the contact angle, compressive strength and pure water flux were examined。 The effects of alumina content and other factors on the properties of the membrane support were analyzed。源C于H优J尔W论R文M网WwW.youeRw.com 原文+QQ752-018766

Keywords：membrane support,  attapulgite,  alumina,  compressive strength

目  录

1课题背景5

1。1 无机膜及膜支撑体5

1。2 无机膜支撑体的特点和要求6

1。3 无机膜支撑体的分析及表征6

1。4 无机膜支撑体的制备7

1。5 课题背景及意义7

2凹土基分离膜的制备与表征7

2。1 实验原料以及仪器8

2。2 支撑体的预处理9

2。3 支撑体的制备9

2。4 支撑体的保存11

3支撑体的表征11

3。1 接触角12

3。2 抗压强度13

3。3 纯水通量14

结 论 16

参考文献  17

致 谢 18

1 课题背景

1。1 无机膜及膜支撑体

多孔陶瓷膜作为一种新的陶瓷材料，因其过滤效率高、机械强度好、稳定性好、耐腐蚀、便于清洗、可再生等优点，被应用于能源、资源、生物工程、化工、环境、冶金、食品、医药等诸多行业领域[1]，且发展日益迅速，应用日益广泛。

陶瓷膜的制备方法，主要有：固态粒子烧结法、阳极氧化法、溶胶-凝胶法、化学气相等。

固态粒子烧结法[2]是先将原料、粘结剂等制成悬浮液，然后在多孔支撑体上涂悬浮液制得膜层，再经过干燥焙烧便可得到氧化铝陶瓷膜。其成型方法有干压成型、注浆成型及挤出成型等。陶瓷膜支撑体一般采用固态粒子烧结制备而成。

实验室中较为常见的是干压成型法，可成型一些形状简单的陶瓷膜。成型后经干燥、高温烧结，使粒子相互连接，形成多孔膜。注浆成型法由于条件不易控制，工业生产则应用较少。挤出成型法则是工业生产中常用的方法。主要制备陶瓷膜管。当然，随着工业不断发展，一些新型的制备方法也随之出现，列入冷冻浇注成型，在此也不多作赘述。

多孔陶瓷膜具有太多优点，如抗污染、寿命长等，发展迅速，广泛的应用各种不同领域。发展前景十分的可观。但是，也具有不可忽视的缺点：制作成本太高，能制作的原料少；工艺复杂、烧制困难，十分不利于商业化；不耐强碱，处理强碱溶液会减短陶瓷膜使用寿命。这些给膜的商业化制备和应用推广带来不可忽视的困难[3]。 

当然随着工艺的不断提高，陶瓷膜一些缺点还是能攻克。所谓瑕不掩瑜，多孔陶瓷膜还是可以凭借其优势在膜界有更大发展，前景广阔。

多孔陶瓷膜由以下三部分组成：