摘 要：本文采用共混改性的方法，将氨基硅烷（KH-103）改性凹土添加到铸膜液中，考察改性凹土对膜分离性能和抗污染性能的影响。实验结果表明，当改性凹土添加量为7%时，膜的渗透性能和亲水性最好，而且改性膜的抗污染能力及机械强度最优；当改性凹土添加量为4%时，改性膜对BSA的静态吸附能力最弱。综合考虑，当改性凹土的添加量为7%时，改性膜的性能最优。77446

毕业论文关 键 词：氨基硅烷(KH-103)改性凹土，聚偏氟乙烯超滤膜，亲水性，分离性能，抗污染性能

Abstract: The attapulgite (ATP) was modified with amino-silane coupling agentsγ-pinyltriaminepropyl-methyldimethoxylsilane (KH-103) by covalent bonding to prepare KH-103-ATP。 The PVDF/ KH-103-ATP hybrid membranes was prepared via a combination of immersion precipitation (IP) and thermally induced phase separation (TIPS) process。 KH-103-ATP was incorporated into PVDF matrix and the influence of modifier amount on membrane properties were investigated in detail。 Experimental results show that as the increasing dosages of the modifier, the water contact angle at 20 °C decreased, the pure water flux (PWF) improved。 The PVDF/KH-103-ATP hybrid membrane exhibited outstanding anti-fouling。 Addtionally, the modified fouling index analyses indicate the serious fouling tendency for pristine membrane was relieved by the increasing KH-103-ATP content。

Keywords: Amino silane modified attapulgite clay (KH - 103), Poly (vinylidene fluoride) (PVDF), ultrafiltration membrane hydrophilic, separating property antifouling property

目  录

1绪论 3

1。1 PVDF膜性能及制备 3

1。2 膜分离 3

1。3 聚偏氟乙烯膜（PVDF）改性 4

1。4 硅烷偶联剂 5

1。5 本文的研究思路及内容 5

2 实验部分 6

2。1 实验药品及仪器 6

2。2 氨基硅烷（KH-103）改性凹土/聚偏氟乙烯超滤膜的制备 7

2。3 膜的机械强度测试 8

2。4 膜的渗透性能及孔径测试 8

2。5 膜对BSA的静态吸附测试 9

2。6 膜的分离性能测试 10

3 实验结果与分析 10

3。1 膜的机械强度分析 10

3。2 膜的渗透性能及孔径分析 11

3。4 膜对BSA的静态吸附分析 12

3。5 膜的分离性能分析 13

结  论 16

参 考 文 献 17

致  谢 19

1绪论

1。1 PVDF膜性能及制备

1。1。1 PVDF膜性能

聚偏氟乙烯由单体偏氟乙烯经悬浮聚合或乳液聚合而得到，它是一种性能较好的成膜材料。PVDF为半结晶聚合物，具有显著的疏水特性，较好的热化学稳定性，优良的机械强度和优秀的成膜能力。PVDF可溶于极性较强的溶剂中，兼有优良的可防制性能可被应用于纺丝制备中空纤维膜；PVDF树脂的优良性在光纤、涂料等各大领域也得到广泛的应用。但是，聚偏氟乙烯强疏水性使其在油水分离和蛋白质分离极易被污染且通量减小，故在该领域受到了制约发展。