摘 要：本文将氨基硅烷（KH-602）改性后的凹土添加到聚偏氟乙烯（PVDF）铸膜液中，通过相转化法制备混合基质超滤膜，对其纯水通量、孔径、红外、电镜等性能进行表征，考察不同改性剂用量对其性能的影响。得出如下结论：对改性凹土红外光谱和混和基质超滤膜断面电镜的分析表明，改性凹土已经成功掺杂到聚偏氟乙烯膜内。PVDF膜在改性后亲水性得到了提高。同时随着KH-602改性凹土添加量的增加，其对应的平均孔径和纯水通量越大。综合考虑，7 wt。%改性凹土添加量膜的性能最优。77449

毕业论文关键词：PVDF膜，超滤膜，相转化法，氨基硅烷 

Abstract：In this article, the modification of amino silane (KH-602) was added to the PVDF casting solution, fabricated hybrid ultrafiltration membrane by phase inversion method。 We studied the effect on pure water flux, pore size, infrared, electron microscope of PVDF membrane, which is influenced by different modifier dosage。 We obtained the following conclusions。 By analyzing the infrared spectrum of the modified attapulgite, the cross section of the hybrid matrix ultrafiltration membrane showed that modified attapulgite had grafted on PVDF successfully。 The hydrophilicity of PVDF membrane was improved after modification。 The more modifier, the grater pore size and pure water flux of PVDF membrane well be。 Comprehensive consideration, the 7 wt。% addition amount of modified attapulgite performs optima。

Keywords： PVDF membrane, ultrafiltration membrane, phase inversion method, amino silane

目   录

1  绪论 3

1。1  聚偏氟乙烯（PVDF） 3

1。2  聚偏氟乙烯（PVDF）膜的制备 3

1。3  PVDF膜的改性 3

1。4  超滤膜 4

1。5  本文的研究思路及内容 4

2  实验部分 5

2。1  实验仪器和试剂 5

2。2  氨基硅烷（KH-602）改性凹土的制备 6

2。3  混合基质超滤膜的制备 6

2。4  混合基质超滤膜的表征 7

3  结果与讨论 8

3。1  红外光谱分析 8

3。2  电镜分析 9

3。3  孔径分析 10

3。4  纯水通量分析 11

结  论 12

参 考 文 献 13

致  谢 15

1  绪论

1。1  聚偏氟乙烯（PVDF）

聚偏氟乙烯是一种结晶性高分子聚合物，常态下为半结晶高分子聚物[1]。迄今为止有α、β、γ、δ和ε等共五种晶体类型，它们的形成条件不同，在一定的条件下（辐射能、热、电场和热的作用下）下可以相互转化。在这五种晶体类型中，β晶体类型最为重要，作为压电和热释电应用的PVDF主要是含β晶体类型[2]。PVDF具有诸多特性，其具有良好的耐紫外线性和高能辐射性，并具有腐蚀性和耐氧化性。因其性能的优越性，在超滤中成为膜材料的首选对象之一[3]。论文网

1。2  聚偏氟乙烯（PVDF）膜的制备