摘要：本文通过将氨基硅烷(KH-103)改性后的凹土添加到聚偏氟乙烯中，通过相转化法制备混合基质超滤膜。考察不同改性剂添加量对PVDF膜形貌、结构以及纯水通量的影响。实验结果表明氨基硅烷（KH-103）能成功的接枝到ATP的表面，并且改性凹土能成功掺杂到膜内。改性凹土加入增大了膜表面孔径和表面粗糙度，但对膜断面微观结构没有产生影响。改性凹土加入改善了PVDF膜的亲水性，使膜通量得到较大提高。79289

毕业论文关键词：聚偏氟乙烯，超滤膜，相转化法，亲水性改性

Abstract: The attapulgite (ATP) was modified with amino-silane coupling agents γ-pinyltriaminepropyl-methyldimethoxylsilane (KH-103) by covalent bonding to prepare KH-103-ATP。 The PVDF/ KH-103-ATP hybrid membranes was prepared via a combination of immersion precipitation (IP) and thermally induced phase separation (TIPS) process。 KH-103-ATP was incorporated into PVDF matrix and the influence of modifier amount on membrane structures and properties were investigated in detail。 The result shows that as the increasing dosages of the modifier, the length of finger-like pores got longer, pure water flux (PWF) improved。 The maximum PWF was about 260 L。 m-2 。h-1, more than two times of the pristine one’s when 7 wt。% of the modifier was added, indicating the improved hydrophilicity and permeability。

Keywords：PVDF, ultrafiltration membrane, phase inversion, modification

目   录

目   录 2

1 绪论 3

1。1 膜的制备方法 3

1。2  PVDF膜表面改性 5

1。3  PVDF膜材料本体改性 6

1。4   本文研究思路 7

2  实验部分 7

2。1  实验仪器和试剂 7

2。2  氨基硅烷(KH-103)改性纳米凹凸棒石吸附材料的制备 8

2。3  改性凹土/聚偏氟乙烯混合基质膜的制备 9

2。4  膜基本性能的分析表征 9

3  结果与讨论 10

3。1  红外色谱图分析 10

3。2  膜的微观结构分析 11

3。3  膜的孔径及孔径分布 13

3。4  膜的水通量 15

结  论 16

参 考 文 献 17

致  谢: 19

1绪论

由于相转化法制备超滤膜操作简单，工艺简便，易于控制膜结构的优点，聚偏氟乙烯超滤膜大多数都是采用相转化法制备的。聚偏氟乙烯超滤膜因具有抗腐蚀、机械性能优良、成本低、制备简便等诸多优点而收到广泛关注关注[1]。但由于聚偏氟乙烯超滤膜自身拥有较强的疏水性，使得超滤膜在使用过程中膜孔容易堵塞，膜体抗污染能力降低，而且很难清理[2~3]。为此，本文将氨基硅烷(KH-103)改性后的凹土添加到聚偏氟乙烯中，通过相转化法制备混合基质超滤膜，探索制备工艺条件对膜形成过程及微结构的影响规律。

1。1膜的制备方法