摘 要：本文通过表面接枝将阳离子表面活性剂十六烷基三甲基溴化铵（CTAB）接枝到凹凸棒石（ATP）表面，制成了CTAB改性凹凸棒石并将其掺杂到聚偏氟乙烯（PVDF）铸膜液中，利用浸没相沉淀相转化法制备CTAB改性凹土混合基质超滤膜，考察不同改性剂用量对PVDF膜红外、形貌、孔径以及纯水通量的影响。实验结果表明：CTAB已成功接枝在ATP的表面；随改性剂添加量的增加，改性膜指状孔变长，膜厚增加，膜孔径越来越大。同时随着改性剂的加入，膜的亲水性提高，纯水通量增大。80005

毕业论文关键词：十六烷基三甲基溴化铵，凹凸棒石（ATP），聚偏氟乙烯，超滤膜，相转化法

Abstract: This paper adopted cetyl trimethyl ammonium bromide (CTAB) to modify attapulgite (ATP) by surface grafting。 Modified attapulgite was added into polyvinylidene fluoride (PVDF) casting solution to prepare ultrafiltration membrane by phase inversion method。 We investigated infrared, morphology, pore size and pure water flux of modified membrane, which was influenced by different modifier’s addition quality。 The results showed that CTAB had grafted successfully on the surface of ATP。 With the modifier’s addition quality increased, the modified membrane’s finger-like pore became shorter, the film thickness raised and the pore size got bigger。 Meanwhile, the modified membrane’s hydrophilic property improved and had greater pure water flux。

Keywords: cetyl trimethyl ammonium bromide(CTAB), attapulgite(ATP), polyvinylidene fluoride (PVDF), ultrafiltration membrane, phase inversion method

目 录

1  引言 3

1。1  凹凸棒石 3

1。2  聚偏氟乙烯（PVDF） 3

1。3  膜和膜分离技术 4

1。4  超滤及超滤膜的制备 4

1。5  相转化制膜法分类 5

1。6  研究的主要内容 6

2  实验部分 6

2。1  实验试剂及仪器 6

2。2  CTAB改性凹土（OATP）复合材料的制备 7

2。3  CTAB改性凹土/聚偏氟乙烯混合基质超滤膜的制备 7

2。4  膜结构及性能的表征 8

3  结果与讨论 9

3。1  FTIR-ATR分析 9

3。2  扫描电镜分析 10

3。3  孔径分析 11

3。4  纯水通量测定 12

结  论 13

参 考 文 献 14

致  谢 17

1  引言

1。1  凹凸棒石

1。1。1  凹凸棒石的性质

凹凸棒石(简称凹土)，是一种层链状结构的含水多孔富镁硅酸盐粘土矿物，理想分子式为Mg5(H2O)4[Si4O10]2(OH)2。

凹凸棒石具有的独特晶体结构赋予其许多特殊的物化性质[1,2]，主要包括：（1）吸附性，取决于凹凸棒石比表面积，表面物化结构和离子状态，因此可以用作助滤剂、净化剂、脱色剂；（2）载体性，由于凹凸棒石具有特殊的孔道结构、界面性质和较大的比表面积，可作优良的催化载体；（3）阳离子交换能力，凹凸棒石表面呈负电性，因此具有交换吸附阳离子的性质；（4）流变性，凹凸棒石在遇到水或极性溶液时迅速张开并解散，表现出良好的胶体性质和水悬浮性质；（5）催化性，凹凸棒石本身是天然的纳米材料，其棒晶具有纳米粒径和大长径比的特点拥有纳米尺寸的孔道，存在大量活性中心，可作催化剂。论文网