摘要：本文以锂电池中的正极材料 Li[Ni0。5Mn0。3Co0。2]O2作为研究课题，研究不同配比以及煅烧条件对其性能影响。通过XRD分析以及电化学工作站分析等手段完成对样品的成分分析、结构分析以及电化学性能分析。尝试通过掺杂铝离子，以及包覆磷酸铁锂外壳的方式，对三元材料Li[Ni0。5Mn0。3Co0。2]O2做掺杂改性以及包覆改性研究，从而进一步提升三元锂电正极材料的电化学性能。800℃下保温12小时的Li[Ni0。5Co0。2Mn0。15Al0。15]O2的样品电化学性能更好。80565

毕业论文关键词： Li[Ni0。5Co0。2 Mn0。3]O2三元正极材料；掺杂改性；循环伏安性能

Study on Modification of LiNi0。5Co0。2Mn0。3O2 as Ternary Material

Abstract Abstract：In this paper, the lithium alloy cathode material Li [Ni0。5Mn0。3Co0。2] O2 as a research topic to study the different ratio and calcination conditions on its performance。 The composition analysis, structural analysis and electrochemical performance analysis of the samples were carried out by means of XRD analysis and electrochemical workstation analysis。 It is attempted to further improve the ternary lithium battery by doping and modifying the ternary material Li [Ni0。5Mn0。3Co0。2] O2 by doping aluminum ions and coating the lithium iron phosphate shell Electrochemical Properties of Cathode Materials。 The electrochemical performance of Li [Ni0。5Co0。2 Mn0。15Al0。15] O2 at 120 ℃ for 12 hours was better。

KeyWords：Li[Ni0。5Mn0。3Co0。2]O2 ternary cathode material；Doping modification；Cyclic voltammetric performance

目录

1绪论 1

1。1 引言 1

1。2 研究意义 1

1。3 锂电池正极材料的发展 1

1。3。1 正极材料的发展历史 1

1。4 Li[Ni0。5Co0。2Mn0。3]O2正极材料简介 2

1。4。1 Li[Ni0。5Co0。2Mn0。3]O2结构特性 2

1。4。1 Li[Ni0。5Co0。2Mn0。3]O2合成方法 3

2 实验部分 5

2。1 实验目的 5

2。2 实验内容 5

2。3 实验试剂 5

2。4 实验仪器 6

2。5 材料的合成制备 6

2。5。1 高温固相法合成Li(Ni0。5Co0。2 Mn0。3)O2 6

2。5。2 研磨法合成LFP@NMC 7

2。5 材料性能分析 7

2。5。1 材料表面性能——XRD（X射线衍射）分析 7

2。6电化学性能 7

2。6。1 电极制备 7

2。6。2 电池的制备 8

2。6。2 交流阻抗测试 8

2。6。3 循环伏安测试 8

3结果与讨论 10

3。1 样品XRD图像分析 10

3。2 电化学性能测试 10

3。2。1掺杂0。15Al离子以及包覆改性性能分析 10

3。2。2 MnO2作为原料实验分析 16

3。2。2掺杂0。05、0。1的Al离子的性能分析