摘 要：铝系的氢氧化物阻燃剂，稳定性好、没有毒性、难挥发、不易析出、不易产生腐蚀性的气体、发烟量比较少等优点，而且资源相当丰富，价格较便宜，符合现今阻燃剂的无卤、少烟、低毒、绿色环保等的发展趋势。trimer作为芯材，利用沉积法，用氢氧化铝作为壁材，对其进行了包覆及改性，通过对trimer进行微胶囊化改性，以来提高它的阻燃效能，从而降低其在高分子材料中的添加量来进一步降低成本。本文还对对包覆的工艺条件做了优化，采用FTIR、XPS、SEM、TG/DTG对微胶囊进行了进一步表征。82139

毕业论文关键词：铝系氢氧化物阻燃剂；trimer；微胶囊

Preparation and Characterization of Metal Aluminum Coated Trimer Microcapsules

Abstract: Aluminum hydroxide flame retardant, good stability, no toxicity, non-volatile, not easy to precipitation, is not easy to generate corrosive gas, hair smoke quantity is little advantage, and resources are quite abundant, cheap, in line with the development trend of modern flame retardant halogen-free, low smoke, low toxicity, green environmental protection and other。 Trimer as the core material, using the deposition method with aluminum hydroxide as the wall material, the were coated and modified, by microencapsulation modification of trimer, improve its flame retardant efficiency, thereby reducing the in polymer materials in addition to further reduce the cost。 In this paper, the coating process conditions were optimized, and FTIR, XPS, SEM and TG/DTG were used for further characterization。

Keywords: Aluminum hydroxide flame retardants; Trimer; Microcapsules

目    录

摘 要 1

引 言 1

1 笼状磷酸酯阻燃剂trimer的合成与表征 2

1。1 实验原理 2

1。2仪器设备 2

1。3主要原料 2

1。4 trimer合成路线 2

1。5 trimer的合成过程 2

1。6 分析测试方法 5

2 Trimer微胶囊制备工艺流程 6

2。1 氢氧化铝包覆trimer微胶囊的制备 6

2。1。1 Al(OH)3包覆trimer微胶囊的条件 7

2。1。2 反应时间对壁材含量的影响 7

2。1。3 pH值对壁材含量的影响 7

2。2 Trimer微胶囊的表征部分 8

2。2。1 Trimer微胶囊的SEM分析 8

2。2。2 Trimer微胶囊的XPS分析 9

2。2。3 Trimer微胶囊FTIR的分析 10

2。2。4 Trimer微胶囊的TG分析 10

3 结 论 12

参考文献 12

致  谢 14

金属铝包覆trimer微胶囊的制备及表征

引 言

三(1-氧代-1-磷杂-2,6,7-三氧杂双环[2。2。2]辛烷-4-亚甲基)磷酸酯是Trimer的化学名，是最新报道的一种新型的膨胀型阻燃剂。它分子中含有三个对称的笼状双环磷酸酯结构，热稳定性好，起始（失重5 %）热分解温度为386。7 ℃；分子中的三个季戊四醇骨架具有良好的成炭性，600 ℃时热失重后的残炭达38。2 %[1]；并且含磷量高达21。2 %，兼具丰富的酸源和炭源；具有不溶于水和绝大多数有机溶剂，几乎不吸湿等优点。李昕[2]等将其与聚磷酸铵和三聚氰胺复配，用于阻燃PP、EVA18及EVA45[3]，取得了较好的阻燃效果。但是，由于成本较高，需要进一步改性。