摘要：一维纳米材料（包括纳米线、纳米棒、纳米管、纳米带等）由于其特别的物理和化学性质今年来成为了研究的热点方向之一。而MnO2做为一种重要的功能材料，近来也成为了研究的热点材料。本论文以羧甲基纤维素为表面活性剂，采用水热法合成了长度在几个微米、宽度在几十纳米的一维α-MnO2纳米线。利用X射线衍射（XRD），扫描电子显微镜（SEM），透射电子显微镜，超导量子干涉仪（SQUID）对干燥后的黑色粉末样品进行了表征和磁性性能的测试。在5K时，所合成的样品显示较弱的铁磁性91334

毕业论文关键词：二氧化锰，磁性，水热

Abstract：One dimensional nanomaterials (including nanowires、nanorods、nanotubes、nanobelts etc) became one of the hottest topic in recent years because of their excellent physical and chemical properties。 As an important functional material, MnO2 received much attentions。 In this paper, we synthesized one dimensional α-MnO2 nanowires under the hydrothermal methods by using carboxymethyl cellulose as surface active agent, the as prepared α-MnO2 was checked by X ray diffraction (XRD), scanning electron microscopy (SEM), transmission  electron microscopy (TEM) and superconducting quantum interference device (SQUID)。 At 5K, a weak ferromagnetism was observed in the as prepared sample。

Keywords：Manganese dioxide，magnetic，Hydrothermal

目 录

1引言 3

2 实验部分 3

2。1样品制备 3

2。2样品表征和磁性性能测试 3

3结果与讨论 4

3。1 样品表征 4

3。2α-MnO2纳米线的磁性 5

结论 9

参考文献 10

致谢 11

1引言来自优I尔Y论S文C网WWw.YoueRw.com 加QQ7520~18766

锰作为重金属的一员，它的含量在地壳中居于第二位，在自然界中与其有关的矿物质至今为止已经发现了50余种，通过锰所构成的氧化物种类也多种多样，其中常见的有黑锰矿(Mn3O4）、软锰矿（MnO2），以及褐锰矿（3Mn3O4•MnSiO4）[1]等。上世纪以来，随着纳米技术的日渐成熟，二氧化锰由于其廉价易得，储量丰富，环境友好等特点，作为纳米材料也越来越受到关注。对其的研究领域多种多样，包括MnO2纳米粉体的制备和将其作为碱锰高能量密度锂电池正极材料，电池正极材料、以及超级电容器电极材料的性能研究等。迄今为止,人们在一维MnO2纳米材料的合成上也已经作出了诸多研究，在合成上，目前二氧化锰的合成方式主要有固相法，溶胶-凝胶模板法，气-固-液（VLS，Vapor-Liqiud-Solid）法，回流法，离子交换法，水热法[2-4]等。而水热法由于其易于控制，操作简单并且能够有效地控制二氧化锰的晶型和形貌尺寸，也备受研究者的青睐。同时二氧化锰的纳米材料也展现了很多特殊的化学性质以及物理性质，如在离子筛、催化材料、分子筛，以及新型磁性材料等领域[9-10]。在本文中我们通过KMnO4和羧甲基纤维素钠表面活性剂水热制备了MnO2纳米线[5-8]，分析通过其表征发现为纯相的α-MnO2，并分别在5K和300k的温度下对其磁性进行了研究，并分析了在1000e磁场作用FC和ZFC的曲线。论文网

2实验部分

2。1样品制备