ANSYS纤维增强硬质聚氨脂材料力学性能研究(2)

时间:2023-02-21 22:22来源:毕业论文
The effects of matrix composition on the mechanical properties of the composites are explored, and the influence of the fiber content on the mechanical properties of the composites is discussed。 On

The effects of matrix composition on the mechanical properties of the composites are explored, and the influence of the fiber content on the mechanical properties of the composites is discussed。 On the basis of this, the preparation process is improved to optimize the mechanical properties of the polyurethane composites。

The preparation technology of fiber reinforced polyurethane is used as a reference for the composite material enhancement。

Keywords  Rigid polyurethane   Reinforced fiber   Mechanical property   Simulation   Orthogonal test

目    次

1  绪论 3

1。1聚氨酯 3

1。1。1 聚氨酯基体 3

1。1。2 聚氨酯复合材料的优点 3

1。2 增强硬质聚氨酯力学性能的研究背景及意义 4

1。3 增强硬质聚氨酯力学性能的国内外研究现状 4

1。4论文研究内容 6

2  纤维增强硬质聚氨酯材料的力学性能仿真 7

2。1  弹塑性材料有限元分析方法 7

2。2  聚氨酯材料模型与参数 7

2。3  几何模型与模拟参数 8

2。4  仿真结果分析 9

2。4。1纤维平行受力方向仿真分析 10

2。4。2纤维垂直受力方向仿真分析 11

3  纤维增强聚氨酯试样制备工艺研究 14

3。1 复合材料制备工艺介绍 14

3。1。1 手糊法 14源-于,优+尔^论=文.网wwW.yOueRw.com 原文+QQ752.018766

3。1。2 模压法 15

3。2  复合材料制备系统 15

3。3 制备工艺研究 17

3。4 工艺实施过程 18

3。4。1  原材料 18

3。4。2  制备的试样 19

3。5 总结与经验 20

4  硬质聚氨酯材料试样力学性能测试及对比分析 21

4。1 制备工艺对复合材料密度的影响 21

4。2 气孔孔径测量结果 23

4。3 压缩实验 24

4。3。1  实验方案 24

4。3。2  压缩实验 25

4。3。3  实验结果与仿真结果的对比 29

4。4 拉伸实验 31

4。4。1  实验方案 31

4。4。2  实验结果 33

结论 34

致  谢 35

参 考 文 献 36

1  绪论

针对纤维增强聚氨酯材料力学性能研究课题,在总结了聚氨酯材料性能基础上,分析了纤维增强聚氨酯材料力学性能的方法。 ANSYS纤维增强硬质聚氨脂材料力学性能研究(2):http://www.youerw.com/wuli/lunwen_140907.html

------分隔线----------------------------
推荐内容