摘要环氧树脂聚合物复合材料常用于生产切削机床床身，修补道路和桥梁等。本课题通过研究不同的空隙率对环氧树脂矿物复合材料性能的影响规律，从而得出最佳的骨料配合比；并在特定的老化条件（紫外耐候老化）下对环氧树脂矿物复合材料的样品进行加速老化处理，通过测试与分析其抗压强度、抗折强度、弯曲应变和弯曲模量，从而研究其稳定性能。通过本试验的研究，我们获得了最佳的骨料配合比；在此基础上研究其老化性能，从而得出环氧树脂矿物复合材料具有优良的稳定性能。22879
毕业论文关键词： 环氧树脂混凝土；孔隙率；老化
Title Research about the enhancement and stability of epoxy resin concrete.
Abstract
The epoxy concrete are always used in the production of cutting machine bed, repairing of the road and bridge. The research is about how porosity influences the properties of the epoxy resin in order to find the most optimal rate of aggregates. Besides, the epoxy resin concrete samples were under specific aging conditions (UV Weathering) to help accelerating aging. The samples were removed at regular intervals to measure its compressive strength, flexural strength, flexural modulus and bending strain to study the stability. After this research, we obtained the most optimal aggregate rate, so as to enhance its performance. Also, we found the property of stability was excellent.
Keywords：epoxy resin concrete ; porosity; aging
目 录
1 引言 1
1.1 环氧树脂的定义和特点 2
1.2 环氧树脂的改性机理 3
1.3 环氧树脂混凝土的国内外研究现状 3
1.4 传统混凝土的老化 4
1.5 高分子聚合物的老化 5
1.6 论文研究的意义 6
2. 实验部分 6
2.1 实验材料 6
2.2 实验仪器和设备 11
2.3 试样制作 13
2.4 性能测试方法 15
2.5 紫外老化方法 15
3 实验结果与分析 17
3.1 不同孔隙率下复合材料的结构与性能 17
3.2 紫外老化对复合材料性能的影响 19
4 实验中存在的问题 22
5 应用前景 23
结 论 24
致 谢 25
参考文献26
1 引言
一般来说，我们能够把聚合物混凝土划成三大类：PIC(Polymer Impregnated Concrete）浸渍混凝土；PMC(Polymer modified Concrete)聚合物改性混凝土以及PC(Polymer Concrete)树脂混凝土。常见的树脂混凝土为环氧树脂混凝土[1]。
1950~1960年，美国的一些商业领域出现了纯聚合物混凝土构件；70年代中期，将其用于修复桥梁及公路。现如今，纯聚合物混凝土层出不穷，像地面排水构件，公路中央隔离栅以及电器构件，机床基础等。
同其他发达国家相比，中国在这方面的研究相对少得多，主要由于技术因素，还受成本、造价这些因素的制约，对聚合物树脂混凝土的研究还仅仅处于起步阶段。不过总的来说，环氧树脂混凝土的研究和应用前景非常广阔[2]。
环氧树脂混凝土与传统混凝土的区别在于，其中的水泥部分，被环氧树脂胶黏剂代替了，后来又向其中加入适当的塑化剂，固化剂以及填料，砂石则作为骨料，经过混合，固化。其具有强度高，耐冲击，耐化学性，耐磨性，耐水性，抗冻性[3]，以及优秀的电气绝缘性，与其他材料粘合强度大，一定程度上弥补了水泥混凝土脆性大，抗裂性小，抗应变小等缺陷。环氧树脂固化之后对化学介质、细菌、大气这些都具有相当强的抵抗能力[4]。 环氧树脂混凝土的强化和稳定性研究:http://www.youerw.com/wuli/lunwen_15713.html