摘要本课题是以硅钢级氧化镁的废弃物为原料，通过煅烧、酸溶、去杂等手段，制备氢氧化镁。再与聚丙烯复合达到阻燃的目的。经过多次试验，对氢氧化镁的制备进行研究与选择，得到最佳的实验方案。实验结果表明：在600℃下煅烧5h能去除碳杂质，以MgO与HCl的摩尔比为1:2.5的浓度，60℃水浴搅拌5h，能更好的是镁离子全部反应。PEG的混合使氢氧化镁的粒度分布更均匀。聚丙烯酸改性使样品的氧指数达到了27，成为了合格的阻燃剂。20038
关键词：硅钢级氧化镁；氢氧化镁；聚丙烯；阻燃剂
Abstract
In this paper, use the rejected material of silicon steel grade magnesium oxide as raw material to prepare magnesium hydroxide by calcinations, acid, miscellaneous and so on. Then composite with polypropylene to achieve the purpose for fire-retardant. After several tests, research and select the magnesium hydroxide’s preparation, get the best experimental program. The results showed that: calcined at 600℃ for 5 hours could remove carbon impurities, the concentration of the 1:2.5-molar-ratio of MgO and HCl, stirred for 5 hours in the 60℃ water bath is the best way to make magnesium the overall reaction. The mixture of PEG with magnesium hydroxide, which can make the particle size be more uniform. Polyacrylic acid modified make the oxygen index reached 27, become a qualified fire retardant.
Key Word: silicon steel grade magnesium oxide, magnesium hydroxide, polypropylene, fire retardant
目录
1 文献综述 1
1.1 高分子材料在建筑材料中的应用 1
1.2 聚丙烯材料的发展及应用 2
1.2.1 聚丙烯材料的发展状态 2
1.2.2 聚丙烯材料的应用 3
1.2.3 聚丙烯材料的缺点及阻燃化 3
1.3 阻燃剂的分类及发展 4
1.3.1 阻燃剂的分类 4
1.3.1 卤化物/Sb2O3阻燃体系 5
1.3.3 磷系阻燃剂 5
1.3.4 磷-溴体系 5
1.3.5 无机阻燃剂 6
1.4 氢氧化镁系无机阻燃剂 6
1.4.1 氢氧化镁阻燃剂的要求 7
1.4.2 氢氧化镁阻燃机理 7
1.4.3 阻燃剂氢氧化镁的制备方法 8
1.5 硅钢用MgO废弃物 9
1.5.1 硅钢简介 9
1.5.2 硅钢用MgO的要求 9
1.5.3 硅钢用MgO废弃物的产生 10
1.5.4 硅钢用MgO废弃物回收再利用的研究意义 10
1.6 选题背景与意义 11
2 实验部分 13
2.1 实验原料及实验仪器 13
2.2 实验过程 14
2.2.1 去除硅钢级氧化镁废弃物中的C等杂质 14
2.2.2 测量溶液中Mg2+浓度 14
2.2.3 亚铁离子浓度测定及去除 15
2.2.4 制备Mg(OH)2 16
2.3 分析表征 16
2.3.1 扫描电镜（SEM） 16
2.3.2 X射线衍射（XRD） 16
2.3.3 UV_Vis透光率分析 16
3 结果与讨论 18
3.1 硅钢氧化镁废弃物表征 18
3.1.1 废弃物结构表征（XRD） 18
3.1.2 废弃物形貌及组成分析 18
3.1.3 硅钢级氧化镁的作用机理研究 19
3.2 硅钢氧化镁废弃物的纯化制备粗Mg2+溶液 20
3.2.1 煅烧时间对除碳的影响 20
3.2.2 硅钢氧化镁废弃物酸溶试验制备粗Mg2+溶液 21 硅钢级MgO废弃物制备的Mg(OH)2及其对PP的阻燃性能的研究:http://www.youerw.com/cailiao/lunwen_11664.html