摘要为了改善聚酰亚胺(PI)的力学、光学等性能，PI复合材料被广泛研究。在本论文中，首先，以4,4-二氨基二苯醚和均苯四甲酸二酐为单体，用N,N-二甲基甲酰胺作为溶剂合成的PI的前驱体，并考察反应时间，反应温度和反应物配比下对PI前驱体的影响；其次，采用溶胶-凝胶法制备二氧化硅含量分别为1%、5%、7.5%、10%、20% 的PI/SiO2复合薄膜；以及二氧化钛含量为0.5%、1%、2%的PI/TiO2复合薄膜。最后，采用XRD、FI-IR、SEM、UV-Vis和接触角测定等方法对所得样品的物相、表面结构、形貌、光学及耐溶解性能等进行了分析。结果表明：得出PI/SiO2/TiO¬2复合薄膜综合性能较优。22714
毕业论文关键词： 聚酰亚胺；二氧化硅；二氧化钛；溶胶-凝胶法
Abstract
PI composites have been widely investigated, in order to improve the mechanical, optical and other properties. In this paper, firstly, the PI precursor was synthesized starting from 4,4’-diaminodiphenyl ether and Pyromellitic dianhydride monomer, with N,N-Dimethylformamide as solvent. During the whole process, the influence of the reaction time, temperature and molar ratio of the reactants on the precursor were explored in detail. Secondly, using the sol-gel method silica content were 1%, 5%, 7.5%, 5%, 20% of the PI/SiO2 composite films ; and titanium dioxide content of 0.5 %, 1% , 2% PI/TiO2 composite film. Finally, a series of measurements including XRD, FT-IR, SEM, UV-Vis and contact angel were employed to test the phase, structure, morphology,and optical and hydrophilic property. The results indicated that the PI/SiO2/TiO2 composite film overall performance is better.
KeyWords： Polyimide；Silica；Titanium dioxide；Sol - gel method
目录
1 绪论 1
1.1 聚酰亚胺 1
1.1.1 聚亚酰胺的概述 1
1.1.2 聚亚酰胺的种类及性能 2
1.1.3 聚酰亚胺的合成及优缺点 2
1.1.4 聚亚酰胺的应用 5
1.2 聚亚酰胺复合材料 6
1.2.1 PI复合材料的分类 6
1.2.2 PI/无机纳米复合材料的制备方法 6
1.2.3 聚酰亚胺复合材料的应用 7
1.3 无机纳米复合薄膜的进展 7
1.3.1 PI薄膜的制备方法 7
1.3.2 PI复合薄膜的应用 8
1.4 PI复合无机纳米粒子 9
1.4.1 用于杂化的纳米SiO2粒子结构与性能 9
1.4.2 用于杂化的纳米TiO2粒子结构与性能 9
1.5 选题的背景与意义 9
2 实验部分 11
2.1 实验原料及实验仪器 11
2.1 实验过程 12
2.1.1 溶液缩聚法制备PAA前躯体 12
2.1.2 原位溶胶-凝胶法制备PI/Si02、PI/TiO2、PI/SiO2/TiO2复合溶液 12
2.1.3 薄膜的旋涂及热处理 13
2.2 测试手段 14
2.2.1 扫描电镜（SEM） 14
2.2.2 X射线衍射（XRD） 14
2.2.3 UV_Vis透光率分析 14
2.2.4 接触角测定 14
2.2.5 显微硬度法测试薄膜厚度和硬度 14
2.2.6 红外吸收光谱分析(FTIR) 15
3 结果与讨论 16
3.1 PI的合成及其性能的研究 16 虫眼型PI/SiO2/TiO2复合薄膜的组装及光学性能研究:http://www.youerw.com/cailiao/lunwen_15441.html