摘要：本实验主要为高性能混炼型聚氨酯硫化体系的研究，重点研究的是硫黄硫化。生胶是用TDI、蓖麻油、1,4-丁二醇、PPG、二乙二醇单乙醚等合成，混炼时则是加入硬脂酸镉、硬脂酸、MBTS、MBT、高耐磨炭黑、硫磺等。实验结果显示随着PPG的含量增多聚氨酯弹性体的硬度、拉伸强度、撕裂强度都渐渐升高，断裂伸长率则随着PPG的含量增多而下降。效果较好的是拉伸强度为21.35MPa，断裂伸长率为254.29%。其它因素对其性能则影响不太明显。30587
毕业论文关键词：聚氨酯；硫化体系；拉伸强度；断裂伸长率；撕裂强度
Research on High Performance millable polyurethane curing system
Abstract:This experiment for the study of high-performance mixing polyurethane curing system, focusing on the sulfur vulcanization. Raw rubber with TDI, castor oil, 1,4-butanediol, PPG, diethylene glycol monomethyl ether synthesis, is added during kneading cadmium stearate, stearic acid, MBTS, MBT, high wear resistance carbon black, sulfur and so on. Experimental results show that with the increase in the content of PPG polyurethane elastomer hardness, tensile strength, tear strength are gradually increased, with the increase in the elongation at break decreased content of PPG. It is better tensile strength 21.35MPa, elongation at break of 254.29 percent. Other factors that affect its performance is not obvious.
Keywords: Polyurethane；curing system；tensile strength；elongation at break；tear strength
目 录 1
1 绪论 1
1.1 聚氨酯弹性体概述 1
1.2 混炼型聚氨酯弹性体 1
1.3 聚氨酯弹性体的分类 2
1.4 聚氨酯弹性体的应用领域 2
1.4.1 耐油密封制品 2
1.4.2 皮革材料 3
1.4.3 聚氨酯纳米复合材料 3
1.4.4 含氟聚氨酯弹性体 3
1.4.5 纳米粘土复合材料 3
1.4.6 橡胶共混 4
1.5 聚氨酯弹性体的发展趋势 4
1.6 课题研究的目的和意义 5
1.7 课题研究内容 5
2 实验过程 7
2.1 混炼型聚氨酯的制备方法 7
2.1.1 主要原材料 7
2.1.2 聚氨酯生胶的合成方法 7
2.1.3 封端TDI 8
2.1.4 封端CO 8
2.1.5 合成生胶 8
2.1.6 胶料塑炼 8
2.1.7 胶料混炼 9
2.1.8 生胶合成注意事项 9
2.2 配方设计 9
2.2.1 生胶配方 9
2.2.2 硫化配方 10
2.3 实验结果与记录 10
2.4 混炼型聚氨酯弹性体的硫化体系 11
2.4.1 异氰酸酯硫化 11
2.4.2 过氧化物硫化 12
2.4.3 硫磺硫化 13
3 实验分析与讨论 14
3.1 生胶对MPU性能的影响 15
3.1.1 生胶对拉伸强度和断裂伸长率的影响 15
3.1.2 生胶对MPU硬度和撕裂强度的影响 16
3.2 硫磺对MPU性能的影响 17
3.3 DM对MPU性能的影响 18
3.4 交联对弹性体性能的影响 19
3.4.1 基团的内聚能 19
3.4.2 氢键 20
3.4.3 结晶性 20
4 结论 21
致谢 22
参考文献 23
1 绪论
1.1 聚氨酯弹性体概述 高性能混炼型聚氨酯硫化体系的研究:http://www.youerw.com/cailiao/lunwen_26379.html