摘要本文中，采用PI、GO与不同含量的ATO粉末进行原位复合，制得PI/GO/ATO复合薄膜并对其进行光学性能的探究。利用扫描电镜探究成膜情况，利用紫外可见分光光度计探究其光学性能，利用红外光谱仪探究其反射红外线的能力。结果表明，当ATO含量为0.6%、GO含量为0.016%时，复合薄膜为无定形态且ATO、GO颗粒分散均匀，无团聚现象。同时复合薄膜的红外反射率达到86%，可见光透过率达到97%，紫外光透过率最低可达0%，即对紫外线的阻隔率达到100%并有明显的减温趋势，因此，此种复合薄膜具备了透明隔热节能效果。31599
毕业论文关键词：ATO；节能薄膜；原位复合
Abstract
In this paper, we use PI, GO with different amounts of ATO powder in situ composite prepared PI / GO / ATO composite film and explore its optical properties.Scanning electron microscopy to explore the deposition situation,Explore its optical performance by the use of UV-visible spectrophotometer.Use infrared spectroscopy to explore the reflection of infrared rays ability.The results show,When the ATO content of 0.6%, GO content of 0.016%, the composite film of amorphous and ATO, GO particles uniformly dispersed without agglomeration.At the same time,the composite film infrared reflectivity of 86%, 97% visible light transmittance, ultraviolet transmittance as low as 0%, that UV blocking rate of 100% and significantly reduced temperature trend,Accordingly, it is a composite film with a transparent insulation energy saving effect.
KeyWords：ATO;Energy conservation film；In-situ polymerization；
目录
1 绪论 1
1.1 节能玻璃 1
1.1.1 节能玻璃研究的目的和意义 1
1.1.2 节能玻璃的分类 2
1.2 纳米ATO薄膜 3
1.2.1 氧化锡锑（ATO） 3
1.2.2 ATO纳米粒子的制备方法 4
1.2.3 ATO纳米粒子的表面改性 5
1.2.4 聚合物基纳米ATO薄膜的制备方法 5
1.2.5 纳米ATO薄膜的研究现状 6
1.3 石墨烯及其衍生物 6
1.3.1 石墨烯 6
1.3.2 氧化石墨烯 7
1.3.3 石墨烯／聚合物复合材料 8
1.4 聚酰亚胺（PI）概述 9
1.4.1 聚酰亚胺（PI） 9
1.5 选题思路 9
2 实验部分 10
2.1 实验原料及实验设备 10
2.2 实验过程 11
2.2.1 溶液缩聚法制备PAA前躯体 11
2.2.2 氧化石墨烯的制备 11
2.2.3 ATO复合薄膜的制备 12
2.2.4 薄膜的成膜及热处理 13
2.3 分析表征 14
2.3.1 扫描电镜 14
2.3.2 X射线衍射分析 14
2.3.3 红外吸收光谱分析 14
2.3.4 拉曼光谱仪 14
2.3.5 原子力显微镜（AFM） 14
2.3.6 透光率分析 15
3 结果与讨论 15
3.1 PI的合成及表征 15
3.1.1 聚酰亚胺前驱体制备 15
3.1.2 反应温度对合成的影响 15
3.1.3 反应时间对合成的影响 16
3.1.4 反应物配比对合成的影响 17
3.1.5 PI合成条件选择 18 ATO隔热透明原位复合薄膜的制备与性能研:http://www.youerw.com/cailiao/lunwen_27814.html