摘要本文是以硅钢级氧化镁的废弃物为原料,通过煅烧、酸溶、去杂等手段,来制备碱式碳酸镁。再将制备的前驱体碱式碳酸镁煅烧成硅钢级氧化镁。实验表明:废弃物在600℃下煅烧5小时能够充分的去除碳物质,接着在60℃的水浴搅锅中搅拌5小时,氧化镁和盐酸比例再1:2.5的时候,镁离子能够彻底的被反应。再利用所得到的高纯度的Mg2+溶液和沉淀剂碳酸氢铵以1:2的比例,添加6%的表面活性剂,在60℃的水浴只中、滴加速率为15rpm的最佳条件下搅拌1小时,制备前驱体碱式碳酸镁。再在950℃的煅烧炉中煅烧2小时获得硅钢级氧化镁。充分实现硅钢级氧化镁废弃物的回收再利用,节能节材。34405
毕业论文关键词:硅钢用氧化镁;前驱体碱式碳酸镁;回收再利用;表面活性剂
Abstract
This article is based on silicon steel grade magnesium oxide waste as raw material, through calcinations, acid dissolution, impurity, to the preparation of basic magnesium carbonate. Then precursor of the preparation of basic magnesium carbonate calcined into silicon steel grade magnesium oxide. Experiment shows that the waste under 600 ℃ calcination 5 hours can fully remove carbon material, then stir in 60 ℃ water bath stirring the pot 5 hours, magnesium and hydrochloric acid ratio 1:2. 5, magnesium ions can completely be reaction. Reuse of high purity Mg2+ solution and precipitating agent ammonium bicarbonate in a ratio of 1:2, add 6% of the surface active agent, in 60 ℃ water bath only, to accelerate the rate of 15 RPM under the best conditions of stirring for 1 hour, the preparation of precursor alkali magnesium carbonate. Again in 950 ℃ calcination of the furnace 2 hours for silicon steel grade magnesium oxide. Fully realize the silicon steel grade magnesium oxide waste recycling, energy saving material.
Key words:Silicon steel grade magnesium oxide;Precursor alkali magnesium carbonate;
Recycling;surface active agent
目 录
1 绪论 1
1.1 概述 1
1.1.1 氧化镁性质及其应用领域 1
1.1.2 氧化镁分类 1
1.1.3 硅钢级氧化镁 2
1.1.4 硅钢级氧化镁的性质要求 2
1.1.5 硅钢级氧化镁的制备方法 3
1.1.6 硅钢级氧化镁的应用 5
1.2 硅钢用氧化镁废弃物 5
1.2.1 硅钢用氧化镁废弃物的产生 5
1.2.2 硅钢用氧化镁废弃物的处理 6
1.3 课题的研究背景与意义 6
1.3.1 国内现状 7
1.3.2 国外现状 7
1.3.3 国内外发展趋势对比 7
1.3.4 本课题研究的基本内容 8
2 实验过程 8
2.1 实验原料及试剂 8
2.2 实验设备 9
2.3 实验过程 9
2.3.1 硅钢级氧化镁废弃物的除杂 9
2.3.2 高纯镁盐的制备 9
2.3.3 硅钢级氧化镁前驱体碱式碳酸镁的制备 10
2.3.4 硅钢级氧化镁的制备 10
2.4 分析表征 11
2.4.1 扫描电子显微镜(SEM) 11
2.4.2 X射线衍射(XRD) 12 取向硅钢用氧化镁的制备及性能研究:http://www.youerw.com/cailiao/lunwen_31891.html