摘要：热处理的本质是相变，而分析热处理相变的一般方法有:热膨胀分析、金相分析、硬度分析、磁性分析等，但是每种方法均有各自的侧重点，准确测量钢铁中的金相组成都需要大型、昂贵的仪器设备，操作也复杂。低合金高碳钢在热处理过程中因为金相成分的改变会产生尺寸的变化，在淬火态与不同回火态下的低合金高碳钢因为组织的变化，会有3%的体积变化，本论文通过热膨胀和二次称重法来证明这种密度变化，同时证明二次称重法从密度的方面对相变分析的可行性。6409
关键字： 热处理；低合金高强度钢；尺寸变化；密度变化；二次称重法
Application of a new method for measurement of martensite in BS950 steel
Abstract：Heat treatment is the essence of phase transformation, and the general method of analysis on heat treatment Transformation: analysis, metallographic analysis, hardness, magnetic properties analysis of thermal expansion, but each method has their own focus, the accurate measurement of iron and Steel Metallurgical in Chengdu need apparatus of large, expensive, operation is complex. Low alloy high carbon steel during heat treatment for metallographic composition changes produce changes in size, in the quenched and tempered at different condition of low alloy high carbon steel for organizational change, volume change will have 3%, the thermal expansion and the two weighing method to prove the density change, and prove the feasibility analysis of the transformation from the density two weighing method.
Key Words: Heat treatment; low alloy high strength steel; dimensional changes; density;Second weighing method
目 录
1 绪论 1
1.1国内外低合金高强度钢的发展概况 1
1.1.1 低合金高强度钢的发展概况[1] 1
1.1.2 低合金高强度钢在我国的发展概况 1
1.1.3 低台金高强度钢在国外的发展 3
1.3低合金钢加工及热处理技术的发展 3
1.3.1奥氏体化 4
1.3.2马氏体淬回火 4
1.4 低合金高强度钢热处理相结构变化 5
1.5 低合金高强度钢热处理尺寸变化 5
1.6 目前对低合金高强度钢马氏体含量的测量方法介绍 5
1.6.1光学显微镜法 5
1.6.2 X射线衍射法 6
1.6.3 磁性法 6
1.6.4 Rietveld方法 7
1.6.5 穆斯堡尔谱法 8
1.6.6 线膨胀方法 9
1.6 宝钢研究院来料BS950高强度低合金钢介绍 9
1.7 本课题研究的目的和意义 10
2 实验部分 10
2.1 实验原料 10
2.2 热处理工艺及设备 10
2.3 二次称重实验方法及设备 12
2.3.1 称量方法 12
2.3.2 对BS950钢进行二次称重 14
2.4 金相组织观察实验 15
2.4.1 实验仪器 15
2.4.2 实验过程 16
2.5 显微硬度测定 16
2.5.1 实验仪器 16
1.5.2 实验过程 16
2.6 热膨胀实验及设备 17
2.6.1 实验仪器 17
2.6.2实验过程 17
3 实验结果与讨论 17
3.1 BS950钢的二次称重结果与分析 17
3.2 金相组织观察结果及分析 19
3.3 显微硬度结果及分析 21
3.4 热膨胀结果及分析 22
4 结论 23 马氏体测量新方法在BS950钢中的应用研究:http://www.youerw.com/cailiao/lunwen_3940.html