本论文采用4004M钎料对3A21铝合金进行真空钎焊。结果表明，较低温度下，钎焊接头的钎料层明显，说明钎料熔化不充分，钎料流动性不强，与母材熔合不明显。较高温度下，较短保温时间，钎焊接头的钎料层不明显，说明钎料基本熔化完全，与母材结合良好，保温时间较长，高温下钎料流动性强容易造成钎料外溢，影响试件外观。在钎焊铝合金复杂结构件时，若无夹具的夹持，容易造成未熔合缺陷。分析表明：钎焊温度625℃，保温时间5min，为最佳铝合金真空钎焊工艺，其强度最高，为68.65MPa。6475
关键词 铝合金 真空钎焊 钎料 夹具 钎焊接头性能 钎焊工艺
毕业设计说明书（论文）外文摘要
Title Experimental research of Aluminum alloy complicated structure vacuum brazing process.
Abstract
4004M solder for the vacuum brazing of 3A21 aluminum alloys was used. The results showed that, under lower temperature, the weld was very clear. It showed that the solder do not melting fully and the mobility of the solder was not strong, fusion with the parent material was not obvious. Under higher temperatures, shorter holding time, the weld was not obvious. It showed that solder melting completely. Longer holding time, under the high temperature, liquid solder easily leaded to spillover and affected the appearance of specimen. When brazed the complicated structure of aluminum alloy, it would easily cause lack of fusion if it had not the fixture. Analysis showed that: brazing temperature of 625℃, holding time of 5min were the best vacuum brazing process for aluminum alloy, with the strength could being 68.65MPa.
Keywords aluminum alloy vacuum brazing solder fixture performance of brazed joints brazing process
目 次
1 引言 1
1.1 课题的意义 1
1.2 铝合金的特点及应用 1
1.3 真空钎焊概述 2
1.4 真空铝钎焊的基本原理 4
1.5 论文研究目的及内容 5
2 试验材料及方法 6
2.1 试验材料 6
2.2 试验设备 8
2.3 工艺及试验方法 9
3 钎焊接头质量分析 12
3.1 钎焊工艺参数的确定 12
3.2 片状铝合金钎焊试样外观形态分析 13
3.3 片状铝合金钎焊试样的力学性能分析 16
3.4 片状铝合金钎焊试样的金相分析 17
3.5 本章小结 19
4 铝波导模拟件的真空钎焊 20
4.1 夹具的设计 20
4.2 加热至610℃，保温15min，钎料厚度0.05mm的模拟件钎焊 21
4.3 加热至625℃，保温25min，钎料厚度0.05mm的模拟件钎焊 22
4.4 本章小结 24
结论 25
致谢 26
参考文献 27
1 引言
1.1 课题的意义
远距离探测雷达，过去主要在军事领域，作为一种防御手段，起着警戒、搜索、跟踪敌机的作用。随着雷达技术的发展，雷达也可作为进攻的辅助手段，如炮瞄、制导、寻的、引爆等，提高了武器的效能。今后，极强功率的雷达可作为微波辐射武器直接杀伤敌方人员和摧毁电子装备，使战争进人“电子兵器”时代。在民用领域，雷达也有着广泛的应用。主要是在气象、天气预报、冰雪厚度测量；地图测绘和国土资源普查；导航、空中交通管制、自动着陆系统以及港口导航等。 铝合金复杂结构件真空钎焊研究+文献综述:http://www.youerw.com/cailiao/lunwen_4052.html