聚乳酸（PLA）/聚醋酸乙烯酯（PVAc）共混体系的形状记忆性能和可降解性能研究

摘要聚乳酸是一种具有良好的生物可降解性、生物相容性的高分子材料，它可利用可再生植物资源作为原料制备而成。本研究利用简单共混的方法制备了新型热塑性聚乳酸/聚醋酸乙烯酯形状记忆材料。研究发现：1. PLLA/PVAc只有一个玻璃化温度，是热力学相容体系。2.PLLA含量变化引起共混体系中PLLA的结晶度的变化。3. PLLA含量到70%时，材料的形状记忆性能最优。4.材料在酸碱度不同的溶液中降解速率快慢顺序为：碱性>酸性>中性。46809

Polylactic acid is a plant utilizing renewable resources as a starting material, prepared by chemical synthesis through biological degradation polymer, having excellent biodegradability and biocompatibility. This work presents a simple strategy to prepare a new type of thermoplastic polylactic acid/polyvinyl acetate shape memory polymers. It was found that PLLA/PVAc is a thermodynamic miscible blend system with only one glass transition temperature. The change of PLLA content causes the change in the blends of PLLA crystallinity. Moreover,when the PLLA content up to 70%, the shape memory properties of the material become to the best.The speed order of material degradation rate in the solution with different pH is Alkaline> Acid> neutral.

毕业论文关键词：微小结晶；降解；形状固定率；形状回复率

Keyword: Tiny Crystals: biodegrade: Shape Fixity: Recovery Ratio

1、前言 4

1.1形状记忆高分子材料定义 4

1.2形状记忆材料类型 4

1.2.1电/磁致型形状记忆高分子 4

1.2.2光致型形状记忆高分子 4

1.2.3化学感应型形状记忆高分子 5

1.2.4热致形状记忆高分子 5

1.3.热致型形状记忆高分子材料的记忆原理 5

1.4聚乳酸的性质及特点 6

1.5聚乳酸类形状记忆聚合物的应用 7

2．实验部分 7

2.1 实验原料 7

2.2 实验仪器、设备 7

2.3 样品制备 8

2.4 性能测试 8

2.4.1形状记忆性能测试 8

2.4.2可降解性能测试 9

3.结果与分析 9

3.1动态粘弹分析（DMA） 9

3.2 热分析（DSC） 11

3.3 形状记忆性能测试 11

3.4 可降解性能测试 13

4.结论 14

参考文献 14

致谢 15

1、前言

1.1形状记忆高分子材料定义

形状记忆高分子材料(Shape Memory Polymer )，简称SMP。“形状记忆”是指具有一定形状的制品，经过形变并定形后，在特定的外部条件刺激下，能够自动恢复成原始形状的现象[1]。外部条件刺激可以是热、化学、机械、光、磁或电等，形状记忆材料对这些触发条件做出响应，从而改变材料原本的技术参数，如形状、位置、应变、硬度、频率、动态或静态特征等[2]。由于形状记忆材料具有众多优异的性能，加上其本身容易和其他材料相结合，形成复合材料，所以其发展越来越受到重视。形状记忆高分子材料作为一种功能性的高分子材料，是高分子材料研究、开发、应用的一个新分支，因为其具有变形量大、重量轻、柔韧性良好、价格便宜、加工性好等特点，渐渐地在材料研究领域扮演着重要角色。聚乳酸（PLA）/聚醋酸乙烯酯（PVAc）共混体系的形状记忆性能和可降解性能研究:http://www.youerw.com/cailiao/lunwen_48619.html