摘要本文以Zn(NO3)2·6H2O、Al(NO3)3·9H2O、EDTA（C10H16N2O8）、C6H8O7·H2O、NH4NO3为原料，采用低温燃烧合成方法，制备粉体；然后再经过研磨、成型、干燥、低温烧成等工艺制备出ZnAl2O4陶瓷。通过对烧失量、烧成收缩率、气孔率、吸水率的计算及物相组成、显微结构等分析，研究前驱体中外加C6H8O7·H2O（100、120、150、180mol%）对铝酸锌纳米粉体烧结性能的影响。52625

结果表明: ZnAl2O4纳米粉体纯度高，粒径小，易团聚。从整体来看，随着前驱体中C6H8O7·H2O量的增加，烧失量、烧成收缩减小，气孔率、吸水率呈现增长趋势。

毕业论文关键词：ZnAl2O4；纳米粉体；低温燃烧合成

Abstract

In this paper，the powder was prepared using Zn(NO3)2·6H2O、Al(NO3)3·9H2O、EDTA（C10H16N2O8）、C6H8O7·H2O、NH4NO3 as starting materials via low temperature combustion synthesis. ZnAl2O4 ceramic were prepared by grinding, molding, drying, and low-temperature sintering. Phase composition and microstructure were analyzed. The effects of C6H8O7·H2O (100,120,150,180 mol%) addition in precursors on sintering properties of ZnAl2O4 nano powders were studied. 

Result showed：ZnAl2O4 nano powders have high purity, small size and easy agglomeration. Overall, with increasing amounts of C6H8O7·H2O in the precursors, the LOI and firing shrinkage decreased, open porosity and water absorption increased. 

Keywords: ZnAl2O4；Nano powders；Low temperature combustion synthesis 

目  录

第一章 引言 1

 1.1课题的背景和意义 1

 1.2 ZnAl2O4纳米粉体的国内外研究进展 2

 1.3 ZnAl2O4纳米粉体的应用 3

  1.3.1 光电材料 3

  1.3.2 催化剂载体 3

  1.3.3 生物材料 4

  1.3.4 陶瓷材料 4

  1.3.5 传感器材料 4

 1.4 ZnAl2O4纳米粉体的制备方法 5

  1.4.1 沉淀法 5

  1.4.2 化学气相沉积法（CVD） 5

  1.4.3 溶胶—凝胶法 6

  1.4.4 水热法 6

  1.4.5有机配合物前驱体法 7

  1.4.6微乳液法 7

  1.4.7自蔓延高温合成 (SHS) 工艺 7

 1.5 本课题的研究内容 8

第二章 实验方案及测试方法 9

 2.1实验原料及仪器 9

 2.2实验方案 10

  2.2.1实验原理 11

 2.3性能的测试与表征 13

  2.3.1 烧失率、烧成收缩率的测定 13

  2.3.2吸水率、气孔率的测定 13

  2.3.3 试样的物相分析 14

  2.3.4 试样的形貌分析 15

第三章 ZnAl2O4纳米粉体合成和烧结性能 16

 3.1 ZnAl2O4纳米粉体的物相和显微结构 柠檬酸对铝酸锌纳米粉体烧结性能的影响:http://www.youerw.com/cailiao/lunwen_56588.html