摘要本文主要研究10mm厚6061铝合金薄板与直径16mm的6061铝合金螺柱之间的感应加热钎焊连接工艺。本文主要分析了几种不同造型的石墨环对于焊接效果的影响，几种不同造型的底板对于焊接效果的影响，通过接头的抗剪切强度试验、宏/微观组织分析和焊缝硬度试验来比较各项优劣。得出最佳工艺是在1600w的功率下加热1-2min，石墨环的最佳形式为内设台阶形，底板的最佳形式为带凹槽形。67690

在最佳工艺基础上完成的焊件表面成型良好，焊缝熔合情况良好，具有较好的接头抗剪强度等力学性能。

毕业论文关键词：铝合金，螺柱，钎焊，石墨环

毕业设计说明书（论文）外文摘要

Title The Study of High strength aluminum alloy brazing process with stud

Abstract

This paper mainly studies the induction heating brazing process in 10mm thick 6061 aluminum alloy sheet with a diameter of 16mm stud.This paper analyzes several different shapes of graphite ring for welding effect, the shape of the floor for several different welding effect, through the joint shear strength test, the macro / micro organizational analysis and weld hardness test to compare the pros and cons. The optimum power is 1600w heating 1-2min, the best form of graphite ring stepped features, the best form of plate-shaped recess for the band.

Under the optimum based on the completion of the weld surface good shape, weld fusion in good condition, the shear strength is good, can be said to have good performance.

Keywords：Aluminum alloy, Stud, Brazing, Graphite ring

目次

1绪论 1

1.1 选题背景及意义 1

1.2铝合金螺柱焊接技术 1

1.3铝合金钎焊技术 2

1.4感应加热技术 3

1.5铝合金螺柱钎焊难点 5

1.6本课题主要研究内容 5

2实验材料与设备 7

2.1 实验材料 7

2.2 实验设备 13

3铝合金螺柱钎焊工艺研究 16

3.1平面底板的试验方式及结果 16

3.2 带凹槽底板的试验方式及结果 18

3.3 带凸台底板的试验方式及结果 21

3.4工艺参数总结 24

3.5现存问题研究 25

结论 26

致谢 27

参考文献 28

1绪论

1.1 选题背景及意义

伴随着现代工业的急速发展，螺柱的使用范围越来越广，使用量也越来越大。螺柱焊接技术有着效率高、接头质量可靠、操作简便、成本低廉等众多优点，可替代铆接、钻孔等螺柱的连接工艺，可焊接各种不同材质的金属材料。

高强铝合金有优良的物理性能、力学性能，而且还具有优良的成形性与焊接性，因此在核工业、航天、军工等各种方面有着广泛的应用。在高强铝合金焊接的领域，钎焊占有着十分重要的地位。而且钎焊有着具有钎焊件变形小、尺寸精度高、有良好的工作环境和相对稳定平均的焊接接头质量的优点。在焊接大直径铝合金螺柱时，传统焊接方式不能保证很好的接头质量，且存在焊接效率低的问题，所以改进工艺考虑螺柱钎焊的方式。 10mm厚6061高强铝合金与螺柱钎焊工艺试验研究:http://www.youerw.com/cailiao/lunwen_75959.html