摘要：由于钒氧化物存在多种价态，具有优异的光学、电学和磁学性能。其中VO2具有热致相变特性，会随着温度的变化发生相转变，并且会伴有光、电和磁的突变，这一特殊性能为VO2提供了广阔的研究价值。本文主要通过改变水热法的反应条件来调控VO2纳米材料的形貌特征，成功制备出了纳米微球颗粒、纳米线及薄膜材料，主要应用于光储能原件、光电开光、防涂材料和智能窗等领域。77912

毕业论文关键词：水热法；二氧化钒；微球颗粒；纳米线 ；薄膜

Preparation and Properties of Vanadium Oxide Nanomaterials and Photoelectric Thin Films

Abstract: Because vanadium exists in a variety of valence states in vanadium oxide, It has excellent optical, electrical and magnetic properties。 Where VO2 has a thermally induced phase transition characteristic, The material will change with the temperature phase transition, and will be accompanied by light, electricity and magnetic mutation, and will be accompanied by light, electricity and magnetic mutation, This special performance for VO2 provides a broad research value。 The morphological characteristics of VO2 nanomaterials were controlled by changing the reaction conditions of hydrothermal method in this study。 Nanometer microspheres, nanowires and thin film materials were successfully prepared in this experiment。 Mainly used in optical energy storage components, photoelectric switches, anti-coated materials and intelligent windows and other fields。

Key words: hydrothermal method; Vanadium dioxide; Nanoparticles; nanowire; film

目录

1引言 1

1。1 VO2材料的概述 1

1。2 氧化钒化合物的结构及性质 1

1。3 VO2纳米晶体结构及其特性 2

1。4氧化钒纳米材料的制备 3

1。4。1一维氧化钒纳米材料 3

1。4。2氧化钒二维材料 3

1。4。3 二氧化钒的应用前景 4

2实验部分 5

2。1 实验试剂和仪器 5

2。1。1实验试剂 5

2。1。2实验仪器 5

2。2 VO2微球颗粒的制备 6

2。3 VO2纳米线的制备 7

2。4 VO2薄膜的制备 8

2。4。1前驱体的合成 8

2。4。2 薄膜的制备 9

2。4。3 VO2薄膜流程图 9

2。5样品的测试和表征 9

2。5。1 X射线衍射(XRD，X-Ray Diffraction)测试 9

2。5。2 扫描电子显微镜（Scanning Electron Microscope，SEM） 10

2。5。3 吸收光谱测试 10

3 结果与讨论 10

3。1 VO2微球颗粒性质的表征 11

3。1。1 VO2纳米微球颗粒的表面形貌分析 11

3。1。2 X射线衍射（XRD）测试分析 13

3。 1。3吸收光谱测试分析 14

3。1。4 小结 14

3。2 VO2纳米线性质的表征 氧化钒纳米材料和光电薄膜的制备及其性质研究:http://www.youerw.com/cailiao/lunwen_89638.html