摘要本试验通过溶胶-凝胶的制备方法，分别制备出CoFe2O4 、BaTiO3的前驱体，通过马弗炉的煅烧得到CoFe2O4、BaTiO3的粉体；然后，分别在不同的摩尔比（1：9、2：8、3：7、4：6、5：5）下进行混合，以无水乙醇为研磨剂，经球磨后，复合得到CoFe2O4 /BaTiO3混合粉末；粉体经过压片成型、微波辅助烧结等过程得到CoFe2O4 /BaTiO3块状复合材料。

通过TG-DSC分析对CoFe2O4前驱体、BaTiO3前驱体测试并保证样品的成功，保证后续试验研究的进行。最后得到CoFe2O4/BaTiO3块状复合材料，经过XRD的检测分析样品及探讨不同复合摩尔比样品的区别。78833

毕业论文关键词： 多铁复合材料；CoFe2O4/BaTiO3；铁电性；铁磁性；微波烧结

Abstract In this study, CoFe2O4 and BaTiO3 precursors were prepared by sol-gel preparation method。 CoFe2O4 and BaTiO3 powders were obtained by calcination of muffle furnace。 Then, the powders were prepared at different molar ratios (1: 9、2：8、3：7、4：6、5：5） The CoFe2O4/BaTiO3 mixed powders were obtained by ball milling, and the powder was subjected to the process of forming and microwave-assisted sintering to obtain CoFe2O4/BaTiO3 mixed powder。 The CoFe2O4 precursor and the BaTiO3 precursor were tested by TG-DSC and the success of the samples was ensured to ensure the follow-up test。 Finally, CoFe2O4/BaTiO3 bulk composites were obtained。 The samples were analyzed by XRD and the difference of different composite molar ratios was discussed。

Key words: Multi - iron composites, CoFe2O4/BaTiO3, Ferroelectric, Ferromagnetic, Microwave sintering

目录

摘要 i

Abstract i

1、绪论 1

1。1研究背景 1

1。2多铁材料的分类 1

1。2。1单相多铁材料的局限性 1

1。2。2复合多铁材料 1

1。3磁电耦合效应 2

1。4 CoFe2O4和铁电材料 4

1。5 BaTiO3和铁磁材料 5

1。6微波烧结 6

1。7微波烧结和普通烧结的比较 7

1。8研究的重要性及研究内容 7

1。8。1研究意义 7

1。8。2研究内容 8

1。8。3对样品检测 8

1。9本章小结 8

2、实验部分 8

2。1实验试剂 8

2。2实验仪器 9

2。3溶胶凝胶方法 9

2。4实验样品的表征方法 10

2。4。1 x射线衍射分析 10

2。4。2铁电体性能测试 10

2。4。3铁磁性能的测试 10

2。5实验流程 10

2。5。1实验准备 10

2。5。2制备铁磁相CoFe2O4粉体 10

2。5。3制备铁电相BaTiO3粉体 12

2。5。4复合陶瓷的制备 13

2。6本章小结 14