中红外POBC多晶粉的合成与性能研究

摘要：本研究基于中红外非光学晶体Pb17O8Cl18（POC）和PbO-PbBr2（POB）二元体系，通过少量掺杂PbBr2，让同为卤素元素的Br原子取代Cl原子，获得POBC材料；此外，通过研究PbO-PbBr2-PbCl2三元系，获得不同比例的PbCl2、PbBr2的POBC固溶体，然后对两种实验结果进行测试。我们采用固相制备法制备POBC多晶料，在440℃下进行煅烧，获得POBC多晶原料，对其进行x-射线粉末衍射、扫描示差热分析、紫外-可见-近红外分光光度计等研究POBC材料的相关性能。82081

毕业论文关键词：非线性光学晶体；固相合成；POBC晶体

Synthesis and Properties of Infrared POBC Polycrystalline Powders Abstract

Abstract：In this study, POBC materials were obtained by replacing the Br atom with br atom as the halogen element by a small amount of PbBr2 doped with Pb1O8Cl18 (POC) and PbO-PbBr2 (POB) binary system。 In addition, -PbBr2-PbCl2 ternary system, different concentrations of PbCl2, PbBr2 POBC solid solution, and then the two experimental results were tested。 The POBC polycrystals were prepared by solid phase preparation and calcined at 440 ℃ to obtain POBC polycrystalline materials。 X-ray powder diffraction, scanning differential thermal analysis, UV-visible-near infrared spectrophotometer POBC material related performance。

Keywords: nonlinear optical crystal, solid phase synthesis, POBC crystals

1 绪论 1

1。2 非线性光学晶体材料概述 1

1。3 非线性光学晶体材料研究现状 1

1。4 非线性光学晶体发展趋势 2

1。5 研究目的及意义 3

2 实验原理 4

2。1 固相反应合成法原理 4

2。2 自发成核法生长POBC晶体 4

2。2。1 结晶过程的驱动力 5

3 实验内容及步骤 7

3。1 POBC的设计思路 7

3。2 POBC的合成 8

3。3 POBC多晶料原料合成原理及所需量 8

3。4 实验所用化学试剂 10

3。5 实验所用仪器 11

4 结果与讨论 12

4。1 POBC多晶料合成过程问题 12

4。2 自发成核图 13

4。3 POBC多晶料的XRD分析 14

4。4 POB的TG-DSC分析 15

4。5 扫描电镜分析 16

4。6 POBC多晶料的吸光度及分析 17

致谢 18

参考文献 19

1 绪论

1961年Franken等发现了晶体的非线性光学效应后，科学家就认识到非线性光学晶体是实现激光变频的主要材料，从而便开始了寻找非线性光学晶体材料的漫长旅途。近五十年来，大量新型非线性光学晶体不断被发现，从化学的角度来分类，非线性光学晶体分为两类，一类是无机非线性光学晶体，如半导体型非线性光学晶体和无机含氧酸盐类晶体(包括硼酸盐、磷酸盐、碘酸盐、妮酸盐和钦酸盐等)等，另一类是有机非线性光学晶体，如有机化合物和金属有机配合物等晶体以及有机聚合物材料等。中红外POBC多晶粉的合成与性能研究:http://www.youerw.com/cailiao/lunwen_96189.html