摘要本文对石墨的结构、性能及其应用研究进行了综述，并对其发展趋势作了展望。
以石墨，粘合剂，溶剂水制备了导电石墨乳。考察了石墨和粘合剂的配比分别对石墨乳导电性的影响,得出在胶的量为16%，石墨最佳配比范围为4%~6%时所得胶体体积电阻率最好。该石墨乳具有造价低，导电性好等优点。总结分析了石墨乳材料在电池，电路，电磁波屏蔽，抗静电，高温防腐等领域的研究现状和应用前景。21440
关键词:  石墨乳  粘合剂  导电性
毕业设计说明书（论文）外文摘要
Title    Preparation of ultrafine  graphite  colloid                  
Abstract
In this paper, the structure, properties and application of graphite were reviewed and prospects for its development trend  are made.Graphite, adhesives, solvents water together prepare conductive graphite colloid.
Examines the impact of the ratio of graphite and binder on conductivity of graphite colloid.when the amount of 16% of plastic, graphite best ratio in the range of 4% to 6%,the resulting colloid volume resistivity is the best.The graphite colloid has the advantage of low cost, good conductivity, etc.Summarizes and analyzes the research status and prospects of graphite
colloid material in the battery, circuit, electromagnetic shielding, antistatic, high temperature corrosion and other fields.
Keywords:    graphite colloid    binder    conductivity

目   录
1 绪论    1
1.1 本课题的研究内容    1
1.1.1  实验目的与意义    1
1.1.1  实验方法的改进与具体实施    1
1.2 石墨    1
1.2.1  膨胀石墨    3
1.2.2  石墨层间化合物    3
1.2.3   导电石墨乳    4
1.3 胶体概述    4
1.3.1 分散体系的分类    4
1.3.2  影响聚沉的主要因素    5
1.4 石墨乳概述    7
1.4.1 石墨乳的性质    8
1.5 导电机理    10
1.6 国内外应用    12
2 实验部分    15
2.1 实验仪器    15
2.3 实验流程图    15
2.4  实验结果    16
结  论    18
致谢    19
参考文献20
 1 绪论 
1.1 本课题的研究内容
1.1.1  实验目的与意义
本实验旨在提供一种导电性优良的石墨导电涂层。以超细石墨，粘合剂，溶剂水为基本实验原料，通过溶液涂布，干燥后即可。经实验证实，该涂层电阻小，实验操作简单，造价低，可初步用于实验室制造。
1.1.1  实验方法的改进与具体实施
与参考文献[14]试验方法对比得知，该实验采用超细石墨为基本原料，代替原有的金属氯化物，提高了导电性，降低了实验造价。与参考文献[15]对比可知，本实验采用超细石墨代替了石墨层间化合物，免去了插层金属的使用如银，铜等，不但减少实验造价，而且减少了实验副反应，如氧化等，提升实验效果。与参考文献[16]对比可知，超细石墨的使用代替了膨胀石墨，减少了加热400℃步骤，节省能源，避免了氯气通流的使用，实验大大简化，并取得一定的实验效果。
1.2 石墨
石墨是碳的一种晶态集合体，呈鳞片状。每一网层间的间隔为320pm，在同一网层中，相邻碳原子的间距为142pm。属优尔方晶系，具有独特完整的层状解理。 超细石墨乳的制备+文献综述:http://www.youerw.com/huaxue/lunwen_13643.html