摘要负载型纳米金催化剂目前是催化领域的一种研究较多的新型催化剂，本文主要研究了在二氧化钛和二氧化硅两种不同载体上，采用不同的方法来制备负载型纳米金催化剂，并研究催化剂在环氧丙烷异构化实验中的催化性能。通过X射线衍射、紫外、扫描电镜、透射电镜对制备的催化剂进行了表征，发现以二氧化硅为载体采用阳离子法制备的催化剂催化性能最佳。又研究了二氧化硅表面经APTS改性后制备得到的催化剂的催化性能，发现其催化性能在高温下（340℃以上）有催化效果。23112
关键字 纳米金 阳离子 二氧化钛 二氧化硅 环氧丙烷 异构化
毕业设计说明书（毕业论文）外文摘要
Title Study on the preparation and the catalytic performance of supported nano-gold catalyst
Abstract
Supported nano-gold catalyst has become a new type of catalyst. In this study nano-gold catalysts supported on TiO2 and SiO2 were prepared by different methods. And the catalysts’ properties were researched through isomerization experiment of propylene oxide. Prepared catalysts were characterized by X-ray diffraction (XRD), UV, electron microscopy (SEM) and transmission electron microscopy(TEM). Results show that SiO2-supported catalysts prepared by cation method prove to be optimal. And the catalytic performance of catalysts supported on APTS-modified SiO2 Surface was researched as well. Results show that these catalysts seem to have good catalytic performance at high temperatures (above 340℃).
Keyword nano-gold; cationic particles; TiO2; SiO2; propylene oxide; isomerization
目 次
1 引言 1
1.1 制备纳米金催化剂 1
1.2 纳米金催化剂的应用 2
1.3 本文的研究内容 3
2 二氧化钛负载纳米金催化剂 4
2.1 实验用药品与仪器 4
2.2 催化剂的制备 5
2.3 环氧丙烷异构化反应 5
2.4 产物分析 7
2.5 紫外表征 7
2.6 XRD图谱表征 7
2.7 HR-TEM表征 8
3 Au-TiO2催化剂的结果与表征 9
3.1 紫外表征 9
3.2 XRD表征 9
3.4 高分辨率透射电镜表征(HR-TEM) 11
3.5 不同制备方法对负载量的影响 13
3.6 催化剂性能评价 13
4 二氧化硅负载纳米金催化剂 16
4.1 中空二氧化硅的制备 16
4.2 纳米金催化剂的制备 16
5 Au-SiO2催化剂的结果与表征 17
5.1 小角XRD 17
5.2 紫外表征 17
5.3 XRD表征 18
5.4 扫描电镜表征（SEM） 20
5.5 高分辨率透射电镜表征（HR-TEM） 20
5.6 催化剂性能评价 21
结 论 23
致 谢 24
参考文献25
1 引言
人们一直把金视为化学惰性金属。将金和其他贵金属作比较，人们很难注意到其所具有的催化潜力。在20世纪80年代后期，日本学者Haruta发现，在三氧化二铁和二氧化钛等氧化物载体上沉积有高低温一氧化碳催化氧化活性的金纳米粒子，且相比之下金独有湿度的增强效应，这也使得传统的金不具有催化活性被打破，由此唤起人们对金的催化特性的关注。近年来，越来越多的研究人员参与到研究开发金催化剂的试验中，人们发现，一些反应（例如NO还原反应、丙烯环氧化反应、烃类氧化反应等）中，金催化剂在催化活性上表现不错[1]。 负载型纳米金催化剂的制备及其催化性能的研究:http://www.youerw.com/huaxue/lunwen_16040.html