摘要：本实验在活性炭表面负载镁、铝、铁复合氧化物制备了一种高效、廉价、安全的新型复合除氟吸附材料。详细考察了煅烧温度和时间、金属离子配比、初始氟离子浓度、吸附时间、pH值等对除氟材料除氟效果的影响。结果表明，该复合材料对氟离子最大吸附容量qm为15.176 mg/g，应用于3个实际高氟井水样的除氟，除氟后水样中的氟离子含量均低于《生活饮用水卫生标准》的限量（1 mg/L），去除率达85%以上。水样经宁夏环境监测中心检测，检测结果与我们所测结果一致。24120
毕业论文关键词： 活性炭复合除氟材料，除氟，饮用水
Activated carbon composite adsorption material removing fluorine ion in the drinking water research
Abstract：This experiment in the activated carbon surface load magnesium, aluminum, and iron compound oxide was prepared by a new type of high efficiency, cheap and safe compound fluoride adsorption material. Detailed the calcining temperature and time, ratio of metal ions, initial fluoride ion concentration, adsorption time, pH value on the effects of fluoride fluoride materials. Results show that the composite material of fluorine ion adsorption capacity of the largest qm is 15.176 mg/g, from non-beryl well applied to the three actual water samples of fluoride, fluoride fluorine ion content of water samples are lower than after "drinking water health standards" limited (1 mg/L), the removal rate of more than 85%.Water detection by ningxia environmental monitoring center, testing results consistent with our measured results.
Keywords：activated carbon；fluoride adsorption material
目 录
1 引言 1
1.1 课题选择意义、研究内容及基础 1
1.1.1 课题选择意义 1
1.1.2 研究基础 2
1.1.3 研究内容 2
1.2 课题研究背景 2
1.2.1吸附剂的种类 2
1.2.2 除氟技术 4
1.2.3 吸附剂的物理性质： 7
1.3 实验方案的确定 8
1.4 本课题的创新点 8
2 实验部分 9
2.1 主要实验仪器 9
2.2 主要实验原料和试剂 9
2.3 实验过程 9
2.3.1 氟离子的测定方法 9
2.3.2 活性炭复合除氟材料的制备 9
2.3.3 吸附实验及吸附量的计算 10
2.3.4样品的测定 10
2.3.5 地下水中常见阴离子对吸附材料除氟的干扰实验 10
2.3.6 活性炭复合吸附材料除氟再生实验 11
3 实验结果与讨论 11
3.1 活性炭复合除氟材料的合成 11
3.1.1不同金属离子配比对活性炭复合材料除氟效果的影响 11
3.1.2不同焙烧温度对吸附材料除氟效果的影响 12
3.2 吸附量的影响因素 13
3.2.1 吸附时间对吸附量的影响 13
3.2.2 氟离子浓度对吸附量的影响及最大吸附量的计算 13
3.2.3 pH值对吸附量的影响 15
3.3地下水中常见阴离子对吸附材料除氟性能的影响 15
3.4 活性炭复合吸附材料的表征 15
3.5吸附材料除氟机理初探 16
3.6 吸附材料应用于实际井水样品的除氟效果 17
3.7吸附材料再生性能 17
4结论 18
致谢 19
参考文献 20
附录 22
1 引言
1.1 课题选择意义、研究内容及基础 活性炭复合吸附材料去除饮用水中氟离子的研究:http://www.youerw.com/huaxue/lunwen_17472.html