摘要：本论文在酸性溶液中，用次磷酸为还原剂，在低碳钢上进行化学镀镍，通过改变镀液的温度，镀液主盐的浓度，添加不同的络合剂对化学镍磷合金镀层的镀层厚度，表面形貌及镀层耐腐蚀性进行实验研究，通过对实验数据讨论分析得出最佳工艺配方是温度为40℃，pH为4，镀液中硫酸镍的浓度为25g/L，次亚磷酸钠的浓度为20g/L，醋酸钠10g/L。化学除油的最佳工艺配方为碳酸钠为30g/L，氢氧化钠为20g/L，磷酸钠为25g/L。非离子表面活性剂为7.5g/L，装载量为1.0dm3，电镀时间为20分钟[1]。最佳工艺配方的镀层最平整光亮，最具有应用前景。5306
关键词：Ni-P合金、次磷酸、络合物、镀层、共沉积
Research of Electroless Plating of Ni-P Alloy Technology Medium Temperature
Abstract:In acidic solution,this paper using phosphoric acid as reducing agent,to electroless plating nickel on the mild steel,by changing the temperature,the main salt concentration, add different complexing agent for chemical plating of nickel phosphorus alloy coating, thickness,suiface morphology and corrosion resistance of coating are discussed and analyzed.The final experimental results obtained temperature to 40℃,pH to 4,the concentration to 25g/L, sodium hypophosphite to 20g/L,sodium acetate to 10g/L,lactic acid to 4mL,sodium carbonate to 30g/L, sodium hydroxide to 20g/L,sodium phosphate to 25g/L,nonionic surfactant to 7.5g/L,loading capacity to 1.0dm3,electroplating time to 20 minutes.The complexing agent is citric acid, the coating is the most smooth and bright,the most promising[2~4].
Keywords: Ni-P alloy;hypophosphorous acid; complex;coating;co-deposition
目录
1 前言 1
1.1 化学镀镍的概述 1
1.1.1 化学镀镍的定义 1
1.1.2 化学镀镍的发展 2
1.1.3 化学镀镍的分类 2
1.1.4 化学镀镍磷合金的应用 3
2 化学镀镍原理 8
2.1 化学镀镍的机理特点 8
2.1.1 原子氢理论 8
2.1.2 氢化物理论 10
2.2 化学镀镍的机理特点 10
2.3 化学镀镍的物理特点 10
2.4 化学镀镍的技术特点 11
3 实验部分 13
3.1 实验原料与仪器 13
3.1.1 实验原料 13
3.1.2 实验仪器 13
3.2 实验设计 13
3.2.1 化学镀前处理 13
3.2.2 化学镀镍的施镀工艺 15
3.2.3 后处理工艺 15
3.3 实验试样性能表征 16
4 实验结果分析与讨论 17
4.1 镀液温度对镀层形貌和镀层性能的影响 17
4.2 镀液pH值对镀层形貌和镀层性能的影响 18
4.3 镀液主盐的浓度对镀层形貌和镀层性能的影响 19
4.4 镀液中不同的络合剂对镀层形貌和镀层性能的影响 21
5 实验结论 24
致谢 25
参考文献 26
1前言
1.1 化学镀镍的概述
化学镀镍是化学镀中发展最快的一种。镀液一般以硫酸镍、乙酸镍等为主盐，次亚磷酸盐、硼氢化钠、硼烷、肼等为还原剂，再添加各种助剂[5]。在酸性溶液或接近常温的中性溶液、碱性溶液中进行作业[6]。
以使用还原剂的不同分为化学镀镍-磷、化学镀镍-硼两大类。镀层在均匀性、耐蚀性、硬度、可焊性、磁性、装饰性上都显示出优越性[7]。 中温化学镀Ni-P合金工艺研究+文献综述:http://www.youerw.com/huaxue/lunwen_2287.html