摘要本文采用溶胶凝胶法，以正硅酸四乙酯（TEOS）、甲基三乙氧基硅烷（MTES）为原料，在催化剂作用下制备硅树脂。实验优化得出硅树脂的最佳合成条件：TEOS、MTES、乙醇和水摩尔比 5:9:8:31，催化剂为盐酸，pH 3～4，反应温度55℃，反应时间 4h。选用亚麻油、三羟基甲基丙烷为主要原料,合成了水性醇酸树脂。通过硅树脂和醇酸树脂的酯化反应，合成了有机硅改性水性醇酸树脂，并用红外光谱（IR)对产物进行了表征。以自制有机硅改性水性醇酸树脂和氨基树脂复配制备改性水性氨基醇酸树脂漆膜，进行了耐酸性、耐碱性、耐盐性等性能的测试。32162
关键词 硅树脂 水性醇酸树脂 有机硅改性 漆膜
毕业论文设计说明书外文摘要
Title Study on Preparation and properties of silicone modified waterborne alkyd resin
Abstract
Under catalysis,silicon resin was prepared form tetraethoxysilane (TEOS) and methyl triethoxysilane (MTES) in sol-gel method.The best synthesis conditions from optimized experimental were as following: mole ratio of TEOS, MTES, C2H5OH and H2O is 5:9:8:31, catalyst is HCl, pH3～4,the reaction temperature is 55℃, and the reaction time is 4h. The water-soluble alkyd resin was prepared by using linseed oil, three hydroxy methyl propane.The waterborne alkyd resin modified by silicone was prepared by esterification of silicon resin with alkyd resin；The infrared spectroscopy (IR) were used to characterize the products.Waterborne amino-alkyd resin baking coatings was prepared by waterborne alkyd resin and amino resin.The performances,such as acid resistance, alkali resistance and salt resistance， were investigated.
Keywords Silicone resin alkyd resin silicon resin modification film
目 次
1 绪论 1
1.1 课题研究背景 1
1.2 有机硅改性水性醇酸树脂的简介 1
1.2.1 醇酸树脂概述 1
1.2.2 水性醇酸树脂 1
1.2.3 醇酸树脂水性化技术 2
1.2.4 有机硅改性醇酸树脂 2
1.3 有机硅改性醇酸树脂的方法 2
1.3.1 物理改性方法 3
1.3.2 化学改性方法 3
1.4 发展现状与展望 3
2 有机硅树脂的制备 4
2.1 实验试剂和仪器 4
2.1.1 实验原料与试剂 4
2.1.2 实验仪器 4
2.1.3 有机硅树脂单体合成机理 4
2.1.4 硅树脂的制备 5
2.1.5 实验装置图 5
2.2 结果与讨论 6
2.2.1 nH2O/nTEOS对硅树脂凝胶时间的影响 6
2.2.2 nH2O/nTEOS对硅树脂粘度的影响 7
2.2.3 催化剂对硅树脂的影响 7
2.2.4 温度对硅树脂凝胶时间的影响 8
2.3 小结 8
3 有机硅改性醇酸树脂的制备 10
3.1 实验试剂与仪器 10
3.2 实验部分 10
3.2.1 醇解反应 10
3.2.2 缩聚反应 11
3.2.3 有机硅改性 11
3.2.4 中和反应 11
3.2.5 对比试验 11
3.3 实验装置图 11
3.4 结果与讨论 12
3.4.1 FT- IR分析 12
3.4.2 植物油的选择 15 有机硅改性水性醇酸树脂的制备及性能研究:http://www.youerw.com/huaxue/lunwen_28616.html