摘要本文采用循环伏安法在氧化钨表面电沉积聚苯胺，制备聚苯胺/氧化钨纳米复合物。通过改变电解液成分、pH值、扫描速率等因素，用循环伏安法测试产物在不同溶液中的电化学活性。结果表明，复合物在低pH电解质溶液中的电化学活性明显高于其在高pH电解质溶液中的电化学活性；随着扫描速率的增大，复合物材料的电化学活性增大；在低pH值的电解质溶液中，峰电流与扫速平方根线性关系良好，说明在低pH条件下，复合物的氧化还原反应为扩散控制。18975
关键词  聚苯胺；复合物；循环伏安法；电化学活性
毕业设计说明书（毕业论文）外文摘要
Title  Preparation of PANI/WO3 nanocomposite
   Abstract
PANI/WO3 nanocomposites were prepared by electrodepositing PANI onto WO3 using cyclic votammetry. In order to study their electrochemical activity by cyclic voltammetry, we change the composition of electrolytes, pH values and scanning rates. The results showed that the electrochemical activity of the composite in the electrolyte of low pH was significantly higher than that of higher pH. And the electrochemical activities of the composite increased with the increasing scanning rates. Futhermore, in electrolyte of low pH values, the peak currents and the square roots of the scan rates were in good linear relationship, which proved that redox of composite were controlled by diffusion.
Keywords   polyaniline; compositie; cyclic voltammetry; electrochemical activity
    目    次

1 序言（或绪论）    1
1.1 聚苯胺的合成    1
1.2 聚苯胺的掺杂    1
1.3 聚苯胺的性能    1
1.4 聚苯胺的应用    2
1.5聚苯胺复合物    2
1.6当前存在的问题    3
1.7循环伏安法    3
2 实验部分    5
2.1 实验试剂与设备    5
2.2 WO3的制备    5
2.3 聚苯胺/氧化钨复合物的制备    6
2.4 性能测试    6
3 结果与讨论    7
3.1 聚苯胺在K2SO4溶液中的电化学活性    8
3.2 聚苯胺在Na2SO4溶液中的电化学活性    10
3.3 聚苯胺在Li2SO4溶液中的电化学活性    11
3.4 聚苯胺在KCl溶液中的电化学活性    13
3.5 聚苯胺在NaCl溶液中的电化学活性    15
3.6 聚苯胺在LiCl溶液中的电化学活性    16
结论    19
致谢    20
参考文献    20
1 序言（或绪论）
常见的人工合成的高分子聚合物导电性一般较差，在过去很长一段时间里，人们一直认为高分子聚合物是绝缘体，随着人们对共轭聚合物结构认识的不断深入，导电高分子这门学科逐渐产生了[1]。 导电高分子是指掺杂后可以由绝缘体转变为导体或者半导体的有机高分子的统称，由于其含有π电子共轭结构，因而表现出电学性能。导电聚合物作为电学材料，具有金属不能比拟的良好的物化特性，因而广泛应用于电子信息工程、国防工程甚至几乎所有的新兴产业以及高新技术领域之中[2]。在众多的导电聚合物中，针对聚乙炔的研究开展的最早也最为深入，而聚苯胺原料价廉易得、合成简单、易加工、化学及空气稳定性好，具有多种形态结构等优点，在催化氧化、生物检测、电子器件制备等方面有着广泛的应用前景[3-8]，成为近些年来导电聚合物研究的热点之一。
1.1 聚苯胺的合成
    聚苯胺的合成方法通常有化学方法和电化学方法，不同聚合方法对聚合物的结构和性能有一定的影响。 聚苯胺氧化钨纳米复合物的制备研究:http://www.youerw.com/huaxue/lunwen_40300.html