摘要PVC加工过程中，由于PVC加工受热脱出HCl导致PVC混料粘度增大，流动性变差，导致PVC在加工中容易粘在加工滚轮上，无法得到良好的成品。
PVC用润滑剂可以有效的解决PVC粘连的现象。PVC用润滑剂分为内润滑剂和外润滑剂。其中内润滑剂是用于减少PVC分子之间的摩擦，而外润滑剂则是减少PVC和加工机械之间的摩擦。47020
本论文主要研究脂肪酸盐对PVC树脂起到的润滑效果。结果表明单一使用脂肪酸盐时，硬脂酸盐外润滑效果最好。复合使用脂肪酸盐时，硬脂酸盐与其他脂肪酸盐复配比例达到3：1时外润滑效果最好
毕业论文关键词：聚氯乙烯；润滑剂；润滑效果
Abstract When the production of PVC, it will emerge HCl when heated PVC mixture.After that the viscosity of PVC increases. It lead PVC easy to stick during processing in the processing rollers and impossible to obtain satisfactory products.
PVC lubricants can effectively solve the PVC adhesion phenomenon. PVC lubricants pided into internal lubricants and external lubricants. Internal lubricants are used to reduce friction between the PVC molecules, and the external lubricants are to reduce friction between the PVC and mechanical.
My thesis research focused on different types of fatty acid salts for PVC lubrication. The results showed that when we used single fatty acid salt, stearate reflected the best external lubrication. When used complex fatty acid salt, stearate and other salts of fatty acids complex ratio of 3: 1, it reflected the best external lubrication in system.
Keywords: PVC; Lubricants ; Lubricating effect.
目录
摘 要 1
1 绪论 2
1.1引言 2
1.2聚氯乙烯 2
1.3润滑剂的选用 3
1.4转矩流变仪 3
1.5本论文研究意义与研究内容 4
2 实验部分 4
2.1实验药品及仪器 4
2.1.1实验药品制备 4
2.1.2实验仪器 6
2.2实验方法 6
2.2.1实验前准备 6
2.2.2实验相关步骤 6
3 结果与讨论 7
3.1单一润滑剂的润滑效果 7
3.1.1同酸根不同金属阳离子润滑剂的润滑效果比较 7
3.1.2同金属阳离子不同酸根润滑剂的润滑效果比较 15
3.2复合润滑剂的润滑效果 16
3.2.1两种同酸根不同金属阳离子润滑剂的润滑效果比较 16
3.2.2两种不同酸根不同金属阳离子润滑剂的润滑效果比较 19
3.3红外谱图分析 20
3.4结果与讨论 21
参考文献 23
致谢 251 绪论
1.1引言
聚氯乙烯（PVC）树脂是五大通用塑料之一，而它以其低成本、高强度、耐腐蚀等特点在日常生活生产中被广泛使用。比如PVC所制成的型材、管材因为性能优良被使用于门窗、管道中；PVC制成的薄膜因为其延展性好，易加工被使用于包装袋、窗帘、雨衣等生活用品中。 脂肪酸钡/锌对PVC润滑作用的研究:http://www.youerw.com/huaxue/lunwen_48936.html