摘要:本文旨在合成模具清洗胶,并对未经硫化的洗模胶与硫化后的胶进行性能的分析与解释。实验得出加了清洗成份的胶料对比没加清洗成份的有非常明显的清模效果。同时,在合成阶段我尝试了多种清洗成份的液体配合剂。发现硬脂酸和硬脂酸钙的加入有利于粘附性的降低,从而易于脱模。钛白粉的加入可以增加其拉伸强度和硫化速率指数。在分析合成胶粘附性时采用的是DMA的夹心剪切模式,测量样品的剪切模量与损耗因子来反应洗胶的粘弹性。发现含清洗配方的洗模胶G’对比无清洗剂的有较大的下降。在试验不同的小料和填料的批次时发现胶料的G’有的增加也有的有减小。70031
毕业论文关键词:洗模胶,DMA,粘模性
Study on Preparation and Adhesion Properties of Mold Cleaning
Abstract: The purpose of this paper is to synthesize mold cleaning glue and analyze and explain the performance of non-vulcanized mold glue and vulcanized rubber. Experiments show that the addition of the cleaning composition of the compound did not add cleaning ingredients have a very clear effect of the clear mold. At the same time, in the synthesis stage I tried a variety of cleaning ingredients of liquid compounding agent. It was found that the addition of stearic acid and calcium stearate favors the decrease in adhesion and thus easy release. The addition of titanium dioxide can increase its tensile strength and vulcanization rate index. In the analysis of the adhesion of synthetic adhesives used in the DMA sandwich shear mode, measuring the shear modulus of the sample and the loss factor to respond to the viscoelasticity of the wash. Found that the cleaning agent with the cleaning agent G' compared to no cleaning agent has a greater decline. In the test of different small materials and fillers of the batch found that the compound of the G' increase also some have reduced.
Key words: mold cleaning rubber, DMA, mold adhesion property
目录
1 绪论 1
1.1 模具清洗胶 1
1.1.1 模具清洗胶研究的目的和意义 1
1.1.3 模具清洗胶的制备技术 2
1.2 主要的清模材料 3
1.2.1 三聚氰胺类 3
1.2.2 清模胶片类 3
1.2.3 三聚氰胺与洗模胶片的对比 4
1.3 模具产生污染的原因和防止方法 4
1.3.1 原因 4
1.3.2 清洗方法 5
1.3.3 硫化仪 7
1.3.4 硫化测试原理 7
1.4 选题背景与意义 8
2 实验部分 9
2.1 实验原料及实验设备 9
2.1.1 原材料 9
2.1.2 仪器设备 9
2.2 基本配方 10
2.3 试样的制备 11
2.3.1 洗模胶的制备 11
2.3.2 模具清洗胶的硫化 11
2.3.3 模压成型 12
2.4 硬度测试 12
2.5 硫化橡胶拉伸 13 模具清洗胶的制备与其粘附性能的研究:http://www.youerw.com/huaxue/lunwen_79146.html