摘要：高比表面积氧化镁具有稳定性好、吸附性强、抗高温、形貌特殊等优点，是合成许多镁试剂的中间体，用途广泛，所以高比表面积纳米氧化镁的可控合成一直备受关注。本文采用水热合成法制备高比表面积氧化镁，考察了搅拌速率、反应温度、溶液pH等因素对纳米氧化镁形貌及其性能的影响，并对产物进行了SEM和BET分析。结果表明：在70℃下，采用乙酸镁和草酸为原料制得草酸镁前驱体，经530℃高温灼烧后得到纳米氧化镁，比表面积可达220 m2/g，其微观形貌呈现均一的立方体。72504

毕业论文关键词：纳米氧化镁，水热合成法，高比表面积，立方体，可控合成

Abstract: The magnesium oxide with high specific surface has a good stability, strong adsorption and special images and resists to high temperature。 As intermediates for the synthesis of nano magnesium reagent, the controllable synthesis of nano magnesium oxide has been closely attracted。 Nano-MgO was synhesised with the hydrothermal method。 Effects of the stirring speed, reaction temperature, solution pH and other factors to the morphology were investigated, and SEM and BET analysis was carried out。 The results showed that magnesium oxalate precursor was produced at 70 ℃ using magnesium acetate and oxalic acid。 After calcanition at 530℃, magnesium oxide was obtained。 The specific surface area is 220 m2/g, and its microstructure uniformity is cube。

Keywords: nano magnesium oxide, hydro-thermal synthesis, high specific surface, cube, controllable synthesis

目   录

1  前言 3

1。1氧化镁应用 3

1。1。1 吸附剂 3

1。1。2 抗菌材料 3

1。1。3 阻燃材料 4

1。1。4 医药方面 4

1。2氧化镁制备方法 4

1。2。1 气相法 4

1。2。2 固相合成法 4

1。2。3 水热合成法 5

1。2。4 溶胶凝胶法 5

1。2。5 其他方法 5

2 实验部分 5

2。1实验仪器与药品 5

2。1。1实验仪器 5

2。1。2实验药品 6

2。2实验步骤 6

3 结果与讨论 7

3。1 SEM分析 7

3。2 BET分析 10

结论 12

参考文献 13

致谢 15

1  前言

众多镁化合物中，氧化镁产量最大、应用最广，在国民经济中具有重要的地位[1]。氧化镁为无味、白色粉末或颗粒，其微观面上存在氧缺陷和镁缺陷[2]，对于氧缺陷，根据留在缺陷里的电子数目(2、1或0)，即分别移去一个中性O原子，1个O-离子或1个二价O2-离子，与之相对应的缺陷分别称为F、F+或F2+。同样对于镁缺陷，分别称为V、V-或V2-，正因这些缺陷的存在使MgO具有强烈化学吸附能力[3]。近年来，有关纳米MgO表面结构与性能的研究引起了广泛关注。朱培怡等[3]研究指出，通过提升纳米MgO 比表面积，能够使其表现出较好的催化与吸附性能。目前市场大多以氯化镁为原料生产纳米氧化镁[4]，采用其他镁盐为原料制备氧化镁的方法还较少，因而开发新方法制备功能性纳米MgO具有一定的研究意义。论文网 高比表面积纳米氧化镁的可控合成:http://www.youerw.com/huaxue/lunwen_82502.html