摘要本次实验实际制备醇酸树脂基高分子防护膜，防护膜要求必须是透明的，并且涂在铝合金表面光滑平整，不影响铝合金板的美观程度。并尝试添加抗腐蚀添加剂，抗老化 添加剂和抗污染添加剂等，使得铝合金防护膜耐腐蚀性能更强。制得耐腐蚀性理想的环 氧树脂型防腐蚀涂料，在环氧清漆的基础上添加了稀释剂松节油、固化剂 2-甲基咪唑和 缓蚀剂二甲亚砜，制得的涂料在海水浸泡后和阳光暴晒下耐腐蚀性理想；实验制得的丙 烯酸酯防腐涂料，在丙烯酸清漆的基础上添加了叔碳酸缩水甘油醚、乙酸丁酯和固化剂， 制得的涂料在海水浸泡后和阳光暴晒下耐腐蚀性理想。 77088
毕业论文关键词 铝合金 防腐蚀 有机膜 醇酸树脂 环氧树脂 丙烯酸酯
毕 业 设 计 说 明 书 外 文 摘 要
Title Alkyd resin-based aluminum protective membrane technology research
Abstract Alkyd resin based polymer protective film of the present experiment the actual preparation, pellicle requirements must be transparent and smooth-coated aluminum alloy surface, it does not affect the aesthetic appearance of the aluminum alloy plate。 And try to add anti-corrosion additives, anti-aging and anti-pollution additives and other additives, so that the corrosion resistance of aluminum alloy pellicle stronger。 Obtained over the corrosion resistance of epoxy-type anti-corrosion coatings, epoxy varnish on the basis of added diluent, turpentine, 2-methylimidazole curing agents and corrosion inhibitors dimethyl sulfoxide, the resulting coating in seawater immersion after sun exposure and lower corrosion resistance over; experiments obtained acrylic anti-corrosion coatings, acrylic lacquer on the basis of added glycidyl versatate, butyl acetate and the curing agent, the resulting coating immersion in seawater and sun under ideal exposure corrosion resistance。
Keywords aluminium alloy anti-corrosion organic membrane alkyd epoxy acrylate
本科毕业设计说明书 第 I 页
目 次
1 绪论 1
1。1 背景 1
1。3 本文研究内容 2
2 醇酸树脂基铝合金防护膜的设计 4
2。1 防腐涂料的理论机理 4
2。2 防腐涂料的机理 4
2。3 环氧树脂防腐涂料和丙烯酸酯防腐涂料的实验设计 4
3 铝合金表面清洗方案 8
3。1 目前金属表面清洗的各种办法 8
3。2 独立设计铝表面清洗办法 9
3。3 原材料及工具… 10
3。4 实验过程及结果… 10
3。5 本章小结… 13
4 环氧树脂型耐腐蚀涂料的具体实验过程 14
4。1 涂膜整体工艺 14
4。2 环氧树脂防腐涂料的最终配方 14
4。3 操作工艺 醇酸树脂基铝合金防护膜技术研究:http://www.youerw.com/huaxue/lunwen_88550.html