蒙脱土/聚乙烯醇渗透汽化膜的制备

摘要：本课题以聚乙烯醇（PVA）和蒙脱土（MMT）为原材料，制作MMT/PVA复合膜，来研究MMT对PVA复合膜的性能影响。通过对含量不同的复合膜的物理化学结构进行表征，并用仪器来分析复合膜的吸水率、热稳定性、结构等性能。结果表明MMT与PVA分子有着很好的相容性，添加不同比例的MMT对复合膜的吸水率，热稳定性，结晶度，微观结构都有不同程度的改善，可以根据对实际应用的具体要求，来掺杂对应比例的MMT，来产生最佳的改性效果。77444

毕业论文关键词：聚乙烯醇，蒙脱土，渗透汽化膜

Abstract:Polyvinyl alcohol (PVA) and montmorillonite (MMT) were selected to prepare MMT / PVA composite pervapration membranes。 Physical and chemical structure of the composite membranes were characterized。 Also, the water absorption of the composite film, thermal stability, structure and other properties were studied。 The results showed that MMT and PVA molecule has a very good compatibility。 Adding different proportions of MMT composite membrane, its water absorption, thermal stability, degree of crystallinity and microstructure were improved。 According to the specific requirements of practical application, the corresponding proportion of the doping MMT was selected。

Keywords:PVA，MMT，Pervapration membrane

1 绪论 4

1。1 渗透汽化膜的研究及应用 4

1。2 聚乙烯醇 5

1。3 蒙脱土 5

1。5 研究内容 6

2 实验 6

2。1 实验材料及试剂 6

2。2 实验步骤 7

2。3 分析方法 7

3 结果与讨论 8

3。1 吸水率的测定 8

3。2 热重分析 9

3。3 差示扫描量热法 10

3。4 红外光谱分析 11

3。5 电镜分析 11

结论 X

参考文献 X

致谢 X

1 绪论

渗透汽化(PV)是一种新型的膜分离技术,原理是液体混合物中不同组分的蒸汽压不同，产生了压力差，并以此为推动力使混合物通过复合膜。因为各组分通过复合膜时的溶解速率与扩散速率存在差异，以达到分离效果[1]。PV因为分离效率高、经济效益好、能耗低、实际放大简便、易操作等优点，被广泛应用于各行各业[2-3]论文网。

1。1 渗透汽化膜的研究及应用

目前，PV分离技术依然一个研究热门。本文基于最近几年来相关文献资料，研究成果，选择合适的材料，进行实验，以希望制备优异性能的汽化渗透膜。

2006年，蔡邦肖等[4]研究了不同种类的PVA复合膜的性能及影响PVA膜性能的因素。研究表明交联剂、支撑膜、高分子网络结构、固载膜对膜的性能有显著影响。

2005年，Santoshkumar D。 Bhat等[5]结合Na + MMT颗粒制备海藻酸钠的新的杂交复合膜。复合膜形成的混合结构比传统原始海藻酸钠膜具有更好的优点。通过加入少量的MMT，产生的微观尺度效果，大大提高了符合膜的选择分离能力。由于MMT优先吸附水分子，可以有效的进行水相与有机相的分离，并且加入了MMT的复合膜具有很高机械强度能够承受反复的PV循环条件。蒙脱土/聚乙烯醇渗透汽化膜的制备:http://www.youerw.com/huaxue/lunwen_89010.html