摘 要：本文以小麦秸秆为原料，沤化得到沼渣。在氮气环境下，通过高温煅烧，制备了生物基炭材料，采用扫描电镜和红外光谱分析等对该材料进行了表征，并对该材料的吸附性能进行了初步研究。分析结果表明，该材料具有一定的孔隙结构。吸附实验表明，小麦秸秆基对甲基橙吸附性能良好,得到了最佳的吸附性能条件。该实验为小麦秸秆的综合利用提供了一种方法。81129
毕业论文关键词：小麦秸秆，活性炭，吸附，甲基橙，酸性品红
Abstract：In this paper, wheat straw was used to prepare biogas by retting method。 The bio-based carbon materials was prepared by high-temperature calcination process, under the nitrogen atmosphere。 The materials was characterized by scanning electron microscopy, infrared spectroscopy, etc。, and the adsorption properties of the material were studied also。 The results showed that the materials has a certain pore structure。 Adsorption experiments showed that the materials has good performance for Methyl Orange, and the best adsorption performance conditions were got also。 This experiment provides a method for the comprehensive utilization of wheat straw。
Keywords: Wheat straw, Activated carbon, Adsorption, Methyl orange, Acid magenta
目 录
1 前言 6
2 小麦秸秆的应用 6
2。1 回归土地的作用 7
2。2 生活中的作用 7
2。3 小麦秸秆的两种主要成分 8
2。3。1 纤维素 8
2。3。2 木质素 8
2。4小麦秸秆基活性炭 9
3 甲基橙和酸性品红 9
3。1 定义 9
3。2 生活中的应用及危害 10
3。2。1 甲基橙的应用及危害 10
3。2。2 酸性品红的应用及危害 11
4 实验 11
4。1 材料试剂及仪器 11
4。2 小麦秸秆活性炭的制备 12
4。3绘制标准曲线 12
4。4 吸附实验 12
4。4。1 吸附时间的影响 13
4。4。2 PH值的影响 13
4。4。3 初始浓度的影响 13
5 结果与讨论 14
5。1 活性炭的表征 14
5。2 活性炭的红外吸收光谱测定 14
5。3 吸附时间的影响 15
5。4 染料溶液PH值的影响 16
5。5 染料溶液初始浓度的影响 18
小 结 20
参考文献 21
致 谢 23
1 前言
小麦秸秆是我国生产量利用率很低的一种农业废弃物，小麦秸秆基活性炭内部具有空隙结构发达、比表面积大、物理化学性质稳定等特点[1]，用扫描电镜、红外光谱分析了其物理结构，甲基橙拥有染料物品的典型的偶氮和醌式结构，酸性品红的代表性在染剂也是较为典范，故本文主要选择小麦秸秆基生物炭吸附甲基橙和酸性品红，从吸附时间、pH 值、初始浓度这三个角度来考察吸附效果的影响。 小麦秸秆基活性炭材料的制备及其吸附实验研究:http://www.youerw.com/huaxue/lunwen_94579.html