摘  要：使用水热法（溶剂热法）合成上转换发光材料NaYF4 : Yb3+, Er3+纳米颗粒，通过改变不同温度，反应体系的不同溶剂，不同助剂，以及不同质量的表面活性剂四个条件来进行实验，使用XRD，SEM，紫外可见漫反射吸收光谱仪以及荧光光谱仪等仪器进行表征。得出实验结论：反应温度180 ℃，反应时间8 h，乙二醇为溶剂，柠檬酸钠为助剂，适量的表面活性剂是最佳条件。有利于生成较均匀较好，发红光性能好的粒子。82006

毕业论文关键词：溶剂热；NaYF4 : Yb, Er；上转换发光材料

The Preparation of Up-conversion Luminescence Materials Using Solvent Thermal Method

Abstract: The up-conversion luminescence NaYF4: Yb3+, Er3+ nanoparticles were prepared by hydro-thermal (solvent thermal) method。 The experiments were carried by changing different temperatures, different solvents reaction system, different additives, and different surfactants。 The products were characterized using XRD, SEM, UV-Vis diffuse reflectance spectroscopy, and fluorescence spectroscopy。 The experimental results show that reaction temperature 180 oC, reaction time 8 h, ethylene glycol as a solvent, sodium citrate as aid, and moderate amount of surfactant are the best synthesis conditions。 Under such conditions, size-uniform nanoparticles emitting red light can be prepared。

Key Words:  Solvothermal; NaYF4: Yb, Er; Conversion luminescence material

目    录

摘  要 1

引  言 1

1 实验部分 2

1。1 实验试剂与仪器 2

1。2 实验过程 3

1。3 样品表征 5

2 结果分析与讨论 5

2。1 物相表征（XRD） 5

2。2 形貌表征（SEM） 6

2。3 样品的紫外可见漫反射吸收光谱 8

2。4 荧光光谱测试 9

3 结  论 10

参考文献 10

致  谢 13

用溶剂热法制备上转换发光纳米材料引  言

上转换发光(Upconversion luminescence)不是普通常见的那种接受能量大于发射能量的发光,它是把低能长波的光子转变为高能短波的光子[1-5]。最近几年来，由于上转换发光材料具有广泛的应用背景而受到关注，因此越来越多的学者去研究它。对于它的研究主要在于设计新的合成方法，开发新的性能，探索出新应用等方面。通过总结得到，纳米材料与传统材料具有很大的区别，这些性质不仅和材料的尺寸大小有关，其次纳米颗粒还能形成不同的形态，比如六方型，立方型，以及纳米球型[6-7]。论文网

掺杂金属离子的稀土纳米原料是具有很多特点的，比如发光它具有很高的强度，又很具环保无毒，发光持续时间长很稳定，这些特点能够检测很多相关的生命体的特性。因为这种材料的触发光是短波的红外光，可以处理光的分散发射的征象，进而用来减低检测背景，提升信噪比，具有着很重要的应用。由于上转换发光材料的特殊的发光机制，因此对于探测早期肿瘤方面具有重要的意义[8-10]。也正是因为这许多的优点使上转换发光纳米材料在医疗等未来高科技上具有非常好的前景。主要用来生物探测，医用治疗以及新能源等方面。上转换材料还具有很多其他的用途，例如固体激光器的应用，太阳能电池的应用以及荧光传感器的研究等等[11-14]。 用溶剂热法制备上转换发光纳米材料:http://www.youerw.com/huaxue/lunwen_96101.html