摘要：本课题从荧光材料LiMgPO4的制备方法、激发发射光谱，发光机理、影响其发光因素以及荧光寿命进行对讨论与研究。Eu2+掺杂LiMgPO4是通过高温固相反应制备获得。相的组成是通过X-射线粉末衍射测量证实。LiMgPO4:Eu2+样品的发射光谱为370到600nm的宽带并且有一个最大发射峰位于495nm，为Eu2+离子的5d→4f的跃迁发射。对共掺杂稀土元素对荧光寿命影响进行了实验与讨论,发现了在共掺杂后荧光寿命τ 1与只掺杂Eu2+相比较减少，而荧光寿命τ 2与只掺杂Eu2+相比较有增加。21936
- 上一篇：载镍炭气凝胶的制备及其脱硫性能的研究
- 下一篇：磁性有序介孔材料对稀土废渣滤液的吸附行为
毕业论文关键词：LiMgPO4；激发发射光谱；荧光寿命图谱；
Study of the spectral characteristics of the LiMgPO4 based light-emitting materials
Abstract： This topic was discussed and studied from preparation method,
excitation-emission spectroscopy, luminescence mechanism and Fluorescence lifetime
spectrum.Eu2+
-doped LiMgPO4 was prepared by a high temperature solid-state
reaction. The phaseformation was confirmed by X-raypowder diffraction
measurements. The excitation-emission spectroscopy of the LiMgPO4 is from 370nm
to 600nm and has the highest peak at 495nm (5d→4f)which is the Transition and
emission of the Eu2+.The defect structures and charge compensation mechanism of Eu3+
doping in LiMgPO4 were discussed.
Key Words: LiMgPO4;excitation-emission spectroscopy;Fluorescence lifetime spectrum
目录
1 绪论 5
1.1 荧光粉发光材料研究的意义和进展. 5
1.2 课题目的. 5
1.3 研究内容. 6
1.4 国内外研究现状. 6
1.5 磷酸镁锂的简介. 6
1.6 LiMgPO4 :Eu2+
发光材料的制备方法 7
1.6.1 高温固相法 7
1.6.2 溶胶-凝胶法 8
1.7 荧光粉发光机理. 8
1.8 影响荧光粉发光的因素. 10
2 实验. 12
2.1 实验原材料和药品. 12
2.2 实验用仪器设备. 12
2.3 制备方法的选择. 13
2.4 试样制备. 13
2.5 工艺优化. 14
2.5.1 烧结温度的影响. 14
2.5.2 Eu2+
掺杂比例的影响 . 14
2.5.3 共掺杂稀土元素离子的影响 15
2.6 测试与表征. 15
3 结果与讨论. 16
3.1 烧结温度的影响. 16
3.2 Eu2+
掺杂比例的影响 17
3.2.1 对物相的影响. 17
3.2.2 对发光性能的影响. 18
3.3 共掺杂稀土元素对发光性能的影响 20
3.3.1 对物相的影响 20
3.3.2 对荧光发射和激发图谱的影响 21
3.3.3 对荧光寿命的影响 22
4 结论. 25
致 谢 26
参考文献 26 1 绪论
本课题研究的 LiMgPO4基发光材料为荧光粉，荧光粉是一种在一定条件
下能发光的无机粉末，有时也叫发光粉，按照激发方式的不同，可分为光致
发光荧光粉、电致发光荧光粉、阴极射线致发光荧光粉和放射性致发光荧光
粉等。由于荧光粉在外界某些条件的激发作用下会发出一些特定颜色的光，
常应用于日光灯、节能灯、LED 灯与显示屏、老式电视机及彩色显示器，PDP
电视，诱蚊的黑光灯，应急指示牌，公路上的指示标记染料等一些领域。
1.1 荧光粉发光材料研究的意义和进展
近些年, 随着新的无机发光材料的不断的被发现以及其性能的提高, 它
的应用也日趋广泛，从而稀土掺杂的发光材料成为了当今研究的热点。由于
稀土化合物的掺杂以及由于其独特的电子结构和跃迁模式而呈现出独特的光
学性能, 已在日常生活以及科学研究领域得到了相当可观的应用, 其还可应