摘    要

极性晶体是制备介电材料的重要前驱体，本文探究性地将聚偏氟乙烯（PVDF）和高k值的碳纳米管（CNTs）进行复合，有望实现高k值的柔性聚合物基复合材料。本工作以PVDF为基体，添加经IL包覆的CNTs，通过辐射和微相分离过程，制备出同时含有均匀分散的CNTs和有机导电纳米微区（PVDF-g-IL）共存的双纳米相复合材料。在辐照前的熔融共混阶段，IL有助于CNTs在基体中的分散；辐照过程中IL接枝到PVDF分子链上；熔融时，接枝有IL的PVDF链发生微相分离，形成纳米微区，而均匀分散的CNTs没有发生二次聚集，因而形成独特的双纳米相复合材料。复合材料具有较好的强度和延展性，同时介电常数高，而介电损耗仍保持在较低的范围内。85218

毕业论文关键词：聚偏氟乙烯、碳纳米管、离子液体、双纳米相复合材料

ABSTRACT

Polar crystals are an important precursor to the preparation of dielectric materials，this paper is expected to product flexible polymer-based composite materials with high k values by combining PVDF with the CNTs which have high k value。 In this work, PVDF has been used as the polymer matrix to fabricate the nanocomposites by incorporation of CNTS and unsaturated ionic liquid (IL)。 With the electron beam irradiation (EBI) and microphase separation processes, it was found that both CNTs and IL-g-PVDF nanodomians were well dispersed in the PVDF matrix。 The binary nanophases nanocomposites are flexible and show good mechanical properties。

Keyword: Poly(vinylidene fluoride) (PVDF);carbon nanotubes (CNTs); ionic liquids (IL); binary nanophases nanocomposites。

目    录

目录

摘    要 I

ABSTRACT II

目    录 IV

1。前言 1

1。1聚偏氟乙烯及其改性研究 1

1。2离子液体在聚合物中的应用 1

1。2。1离子液体简介 1

1。2。2离子液体在聚合物中的应用 2

1。3碳纳米管在聚合物中的应用 2

1。4本课题的提出以及主要研究内容 3

2。实验部分 4

2。1实验试剂 4

2。2实验仪器 4

2。3碳纳米管与纳米微区PVDF/IL-CNTs复合材料的制备 4

2。3。1PVDF/IL-CNTs共混薄膜的制备 4

2。3。2辐射接枝PVDF/IL-CNTs共混薄膜源Q于W优H尔J论K文M网WwW.youeRw.com 原文+QQ75201.,8766 的制备 4

2。3。3碳纳米管与纳米微区PVDF/IL-CNTs共混薄膜的制备 5

2。4实验表征 5

3。结果与讨论 7

3。1IL与CNTs的相互作用 7

3。2形貌研究 8

3。3晶型的表征 8

3。4结晶和熔融行为的表征 10

3。5力学性能 12

4。总结与展望 15

4。1总结 15

4。2展望 16