摘要本论文中利用Gleeble1500试验机主要研究了AZ61镁合金在变形温度为250-400℃，应变速率为0.01-10s-1下的塑性变形行为。研究结果表明：AZ61镁合金在热变形过程中的真应力、峰值应变会随变形温度、应变速率的变化而发生改变。 38129
- 上一篇：纤维状介孔二氧化硅的pH值响应
- 下一篇：Fe-Mn熔体中Mn的活度研究
AZ61镁合金的真应力峰值和峰值应力所对应的应变会随应变速率的降低、变形温度的升高而减小。本文采用双曲正弦函数 关系来描述AZ61镁合金在塑性变形行为过程中的真应力、应变速率和变形温度之间的关系。该合金在塑性变形行为过程中的变形激活能为Q=112.969kJ/mol，应力因子 =0.0105MPa-1，应力指数n=7.23。
变形温度和应变速率可控制AZ61镁合金在塑性变形过程中的动态再结晶。在塑性变形过程中，材料在低温下存在大量孪晶，随着变形温度的升高和应变速率的降低，孪晶数量逐渐减少，并开始动态再结晶，使晶粒细化。
通过AZ61镁合金的塑性变形行为得到的实验数据来建立该材料在热塑性变形行为过程中的热加工图。由热加工图表明，该材料在低温低速和高温中速的变形条件下出现失稳情况。最终得到的最佳热变形条件为变形温度为340-400℃，应变速率为0.01s-1。此时功能转化率为最大值，变形后的材料的性能最好。
毕业论文关键词：AZ61镁合金；真应力；塑性变形行为；热激活能；热加工图；功能转化效率
The thermal deformation behavior and the thermal processing map of AZ61 magnesium alloy
Abstract
The plastic deformation behavior of AZ61 magnesium alloy during different temperatures (250-400℃) and strain rates (0.01-10s-1) are studied on Gleeble-1500 .The results show that the true stress of the material will be varies with deformation conditions changing.
With the lower strain rate and higher deformation temperature , true stress peak and corresponding strain of AZ61 magnesium alloy will significantly reduce. In this paper, the Arrhenius function, ,describe the relationship between the true stress of AZ61 magnesium alloy of different strain rate and temperature during the process of plastic deformation behavior . During the process of plastic deformation behavior,tensile deformation activation energy of this alloy is 112.969kJ/mol ,stress factor α = 0.0105MPa-1, stress exponent n =7.23
The deformation temperature and the strain rate control the nucleation mechanism of DRX during the plastic deformation of AZ61 magnesium alloy. A large number of twins are observed at lower temperature. With temperature rise and strain rate reduce, twins gradually reduce and dynamic re-crystallization finer grain size.
Using the experimental data in plastic deformation behavior of AZ61 magnesium alloy obtained to establish the thermal processing graph during the thermoplastic deformation behavior .The thermal processing graph shows that AZ61 magnesium alloy will be instability under the condition of lower speed at lower temperature and medium speed at higher temperature. Best of hot deformation conditions for the deformation temperature at 340-400℃, strain rate of 0.01s-1.Then, AZ61 magnesium alloy get the maximum conversion rate of the functional and material performance after deformation is best.
Key words：AZ61 magnesium alloy ； thermal processing map；true stress ； plastic deformation behavior ； thermal activation energy ； functional conversion efficiency
目录
第一章 绪论 1
1.1 镁及其合金的概述 1
1.1.1 镁的性质 1
1.1.2镁合金的应用及发展前景 2
1.1.3Mg-Al-Zn系镁合金的概述 2
1.2镁合金的塑性变形 3
1.2.1镁合金塑性变形机制 3
1.2.2镁合金塑性成形工艺 4
1.2.3镁合金的塑性成形的特点 5
-
不同链长聚二甲基硅氧烷...
-
电弧离子镀TiAlN硬质薄膜的制备及性能研究
-
电弧离子镀TiCN硬质薄膜的制备及性能研究
-
稀土元素Dy对合金涂层结构与高温性能的影响
-
金属纳米晶体铁磁转变温度的热力学研究
-
热管/超声协同FSW弱连接的...
-
ZK60表面MAO-ED陶瓷/HA复合生物涂层的制备
NFC协议物理层的软件实现+文献综述
现代简约美式风格在室内家装中的运用
浅析中国古代宗法制度
巴金《激流三部曲》高觉新的悲剧命运
上市公司股权结构对经营绩效的影响研究
高警觉工作人群的元情绪...
C++最短路径算法研究和程序设计
中国传统元素在游戏角色...
g-C3N4光催化剂的制备和光催化性能研究
江苏省某高中学生体质现状的调查研究