摘要采用一步法，在回收聚碳酸酯中添加PET，引入反应性的官能团羧基（—COOH），然后扩链增韧。本文所用扩链剂为RC1，增韧剂分别为RC2和RC3。通过转矩流变仪，以回收聚碳酸酯（r-PC）与PET，RC1，RC2，RC3，按一定的比例做共混实验，制备共混样品。通过对共混样品做万能材料试验机拉伸实验，断裂面电镜扫描分析，结果表明：通过添加PET，使得PET与PC发生反应，引入反应性的官能团羧基（—COOH），可以与扩链剂上面的环氧发生反应，从而达到扩链的作用，起到PC增韧的作用。但核壳结构的增韧剂RC2和RC3的加入，并没有使得体系的断裂伸张率得到提高，反而下降，而添加RC1和PET的r-PC体系具有较好的强度和断裂伸长率。47798
毕业论文关键词：回收聚碳酸酯；转矩流变仪；混炼；增韧。
Abstract
In this paper, small amount of PET and chain extenders have been added into recycled PC (r-PC) to increase the molecular weight of r-PC. It is expected that the PET can react with PC by transesterification reaction and the reactive –COOH groups were introduced to the r-PC. The following chain extender can reactive with –COOH and the molecular weight of r-PC can be increased. It was found that RC2 and RC3 do not increase the mechanical performance of r-PC. However, the cooperation of RC1 and PET improves the mechanical properties of r-PC.
Key Words: r-Polycarbonate ; Torque Rheometer; Kneading ; toughening.
目 录
回收聚碳酸酯（PC）增韧改性的研究 1
摘要 2
1.1引言 5
1.2 PC的结构及性能特点 5
1.2.1 力学性能 6
1.2.2 热性能 6
1.2.3 光学性能 7
1.2.4 电性能 7
1.2.5 耐化学试剂和耐腐蚀性能 7
1.2.6 耐老化和燃烧性能 7
1.2.7 相容性 7
1.2.8 流动性 8
1.3 PC的发展现状及应用 8
1.3.1 建筑材料 8
1.3.2 汽车制造 8
1.3.3 医疗器械 8
1.3.4航空航天 8
1.3.5 包装行业 8
1.3.6电器电子 8
1.3.7 光学透镜 9
1.3.8 光盘器材 9
2 实验部分 10
2.1实验原料与试剂 10
2.2实验仪器、设备 10
2.3样本制备 11
2.4万能材料试验机拉伸试验 11
2.5电镜扫描试验（PESEM） 11
3结果与讨论 12
3.1样本拉伸性能 12
3.2样本拉伸性能曲线图 13
3.3增韧剂的使用 16
3.4探索不同的比例的PET和RC1（GP301）的添加量 17
3.5电镜扫描分析（SEM） 18