摘要：陶瓷膜在水处理，食品行业，能源环境以及生化化工这些领域的应用越来越广泛。陶瓷膜在分离应用中均存在膜易受污染、通量衰减等缺点，严重影响了陶瓷膜的分离效率。通过纳米氧化物颗粒修饰改性能有效提高陶瓷膜的性能。本文以纳米凹土对氧化铝微滤膜改性制备微滤膜，考察涂膜时间以及烧结温度等对微滤膜性能的影响。结果表明，50 s涂膜时间，700 ℃的烧结温度制成膜性能最佳。凹土改性的氧化铝微滤膜对油的截留率大大提高，对水的渗透通量稍微有所减少。此外，膜的抗污染，易清洗能力有所提高。93991

毕业论文关键词：陶瓷膜，纳米凹土，微滤膜

Abstract: At present, ceramic membranes are widely used in water treatment, food industry, energy environment, biochemical and chemical industries。 However, its production costs, high operating costs and membrane pollution problems seriously restrict the further development of membrane technology。 The nano-metal oxide particles could effectively increase the ceramic membrane’s performance。 In this paper, the Al2O3 microfiltration membrane was modified with nano-attapulgite。 The effects of the dip coating time and sintering temperature on microfiltration membrane were studied。 The results showed that the Al2O3 microfiltration membrane modified with the nano-attapulgite, which was prepared under the dip coating time of 50 seconds and sintering temperature of 650℃,had better stable flux。 The rate of retention of the modified alumina microfiltration membrane was greatly improved, and the permeation flux of water was slightly reduced。 In addition, the membrane showed good anti- fouling property。源C于H优J尔W论R文M网WwW.youeRw.com 原文+QQ752-018766

Key words: ceramic membranes, nano-attapulgite, microfiltration membranen

目  录

1 前言 3

1。1 凹凸棒石 3

1。1。1 凹凸棒石的结构 3

1。1。2 凹土的提纯 3

1。1。3 凹土的性能 4

1。2 无机陶瓷膜 4

1。2。1 陶瓷膜的分类 4

1。2。2 无机陶瓷膜特性 4

1。3 陶瓷微滤膜 5

1。3。1 陶瓷微滤膜的制备方法 5

1。3。2 陶瓷微滤膜的改性 6

1。4 本文研究目的及内容 7

2 实验部分 7

2。1 实验仪器及试剂 7

2。2 膜管的预处理 8

2。3 凹土制膜液的配置 9

2。4 膜的制备及性能考察 9

2。5 油水分离过程 10

2。6实验测定和分析方法 10

3 结果与讨论 10

3。1 凹土微滤膜的表征 10

结论 14

参考文献 15

致谢 17

1 前言

1。1 凹凸棒石

1。1。1 凹凸棒石的结构来自优I尔Q论T文D网WWw.YoueRw.com 加QQ7520~18766

凹凸棒石，又被叫做坡缕石，是自然界中一种稀少的矿物资源。1976年在我国江苏省盱眙县内首次发现该矿石，学者许冀泉由其音译和该矿石的晶体结构特征，将其翻译为“凹凸棒石”。中国是凹土的资源大国，仅盱眙地区的粘土总量就达5亿吨，其中优质粘土储量在6700万吨以上[1~2]。