摘要:本课题采用模板法制备纳米球型氧化锌颗粒,用锌盐为原材料,通过催化剂作用以及后期煅烧制备出纳米球型氧化锌颗粒。以紫外吸光性能和粒径大小为指标优化制备工艺,并通过透射电镜和红外光扫描对煅烧前后进行测定。结果表明,制备球型氧化锌颗粒的最佳工艺为,聚合物球粒径为395nm,反应温度为60℃,催化剂用量为200ul,锌盐用量为3%,煅烧时间为3h,煅烧温度为500℃。此时制备出来的球型氧化锌颗粒粒径为647nm左右,紫外吸光性能最优。29438
毕业论文关键词:模板法 纳米球型氧化锌 紫外屏蔽性能
Preparation and Properties of Nano UV Shielding Agent
Abstract: This paper mainly adopts a certain proportion of styrene, ammonium persulfate, acrylic acid, polyvinyl pyrrolidone (PVP) fully stirring and nitrogen into the and oil bath heating to a certain temperature, later joining initiator potassium persulfate, isothermal reaction 10 hours, after centrifugation washing system for preparation of anionic PS template. Take 0.1ps template (solid content is 1%) by adding a certain amount of water, with magnetic stirring heating to 60 ℃, constant temperature reaction 1 hour, with injection machine into a certain amount of Zn(NO3)2•6H2O, isothermal reaction 3 hours, with injection molding machine into a certain amount of ammonia, reaction for 2 hours, centrifugal washing and finally into the muffle furnace up to calcined at a certain temperature for 3 hours. The results showed that the nano zinc oxide hollow spheres of the optimum preparation process for, PS template particle size in 393-399nm, Zn(NO3)2•6H2O dosage for 0.2975g and ammonia of the injection volume 200ul, calcination temperature to 500 ℃, then prepared zinc oxide hollow spheres UV shielding performance is the best.
Keywords: Template Nano-type zinc oxide UV Shielding Agent
目录
1 绪论 1
1.1 纳米材料.. 1
1.1.1 纳米材料的发展 ..1
1.1.2 纳米材料的制备.2
1.1.3 纳米材料的光学性质 2
1.2 紫外屏蔽剂..3
- 上一篇:柠檬油微乳体系的制备与研究
- 下一篇:薄荷香型卷烟的加料加香研究
-
-
-
-
-
-
-
C++最短路径算法研究和程序设计
浅析中国古代宗法制度
上市公司股权结构对经营绩效的影响研究
巴金《激流三部曲》高觉新的悲剧命运
江苏省某高中学生体质现状的调查研究
现代简约美式风格在室内家装中的运用
中国传统元素在游戏角色...
g-C3N4光催化剂的制备和光催化性能研究
NFC协议物理层的软件实现+文献综述
高警觉工作人群的元情绪...