摘要：先用硼酸，氢氧化钠配制成硼砂溶液，再用硼砂，硝酸铈，正丁醇和十二醇在二甲苯作为溶剂的体系中反应生成十二烷氧基硼酸铈，最适宜的反应条件是：硝酸铈和硼砂的摩尔比为2:3，酯化反应时间为0.5h，酯化反应温度为130℃，酯交换反应时间为0.5h，反应得到的产物的最高产率为84.01%。利用红外光谱仪分析产物，并在四球试验机上，测定了十二烷氧基硼酸铈添加到基础油后的摩擦磨损性能及十二烷氧基硼酸铈的添加量对这些性能的影响进行了考察，结果表明，含十二烷氧基硼酸铈1.5%（wt%）时，抗磨效果最适宜。测定基础油、添加1.5%（wt%）十二烷氧基硼酸铈的基础油及添加T202的基础油三者的最大无卡咬负荷PB，结果表明添加1.5%十二烷氧基硼酸铈后基础油的PB值最大。最后测定十二烷氧基硼酸铈与T202复配后的摩擦化学性能以及两者的添加量对基础油的摩擦磨损性能的影响，结果表明，当添加1.5%（wt%）十二烷氧基硼酸铈时和添加1%（wt%）T202复配时，润滑油的抗磨效果较好。9303
- 上一篇：广州市空气质量研究+文献综述
- 下一篇：铜银合金粉的合成+文献综述
关键词：十二烷氧基硼酸铈；合成；润滑油；抗磨减摩
Tribo-chemical Properties and Synthesis on Cerium Dodecoxylborate
Abstract: The borax is the reaction of orthoboric acid and sodium hydroxide,The cerium dodecoxyborate is the reaction of borax,cerium nitrate,butyl alcohol and dodecanol under the xylene system. The better reaction condition is when the mole ratio of cerium nitrate and borax is 2:3, the esterification reaction time is 0.5h, the reaction temperature is 130℃,the transesterification reaction time is 0.5h and the most prolific rate of the product is 84.01%.It’s analyszed on cerium dodecoxyborate with IR . On the four ball machine, it’s shown that antiwear and antifriction characteristic were determined on cerium dodecoxyborate added to base oil,on which properties the addition of cerium dodecoxyborate were investigated. It’s shown that wear the better on results,when the content of cerium dodecoxyborate is 1.5%(wt%). It’s determined the largest non-card bite load PB of base oil, adding 1.5%(wt%) of cerium dodecoxyborate in the base oil and adding the T202's base oil, on results it’s shown that the base oil after adding T202,its PB is maximum. Finally, it’s determined that tribo-chemical characteristic about the compound of cerium dodecoxyborate synergied with T202, the friction and wear performance impact on these two adding amount of base oil.It’s shown that the anti-wear of lubricating oil gains its better effects on results,when add 1.5%(wt%) of cerium dodecoxyborate and add 1%(wt%) of T202 synergied.
Key words: cerium dodecoxyborate;synthesis;lubricants;antiwear and antifriction
目录
1绪论 1
1.1润滑剂 1
1.1.1润滑剂的作用 1
1.1.2润滑机理 2
1.1.3润滑剂的发展 2
1.2润滑油添加剂 3
1.2.1润滑油添加剂的工作原理 3
1.2.2润滑油添加剂的开发 3
1.2.3添加剂的作用 4
1.3硼酸盐润滑油添加剂 4
1.3.1硼元素及其化合物简介 4
1.3.2硼酸盐衍生物 5
1.3.3硼酸盐添加剂的研究进展 6
1.3.3.1硼酸盐添加剂的制备 6
1.3.3.2硼酸盐添加剂的摩擦学性能 7
1.3.3.3硼酸盐添加剂的极压抗磨减摩机制 8
1.3.4硼酸盐润滑油添加剂的发展前景 10
1.4本论文的主要工作和创新点 11
1.4.1本课题的主要工作 11
1.4..2 本课题的创新点 11
-
Cu2+诱导的硼-二吡咯亚甲基...
-
甲基咪唑衍生物荧光配体合成及其性能研究
-
羧基苯甲醛希夫碱合成及配合物性能研究
-
氨基噻吩荧光配体合成及性能研究
-
Zn2GeO4光催化材料的形貌调...
-
基于柔性羧酸配体的MOFs的合成与晶体结构
-
铜基纳米材料的制备及性能研究
上市公司股权结构对经营绩效的影响研究
巴金《激流三部曲》高觉新的悲剧命运
高警觉工作人群的元情绪...
NFC协议物理层的软件实现+文献综述
江苏省某高中学生体质现状的调查研究
C++最短路径算法研究和程序设计
g-C3N4光催化剂的制备和光催化性能研究
现代简约美式风格在室内家装中的运用
中国传统元素在游戏角色...
浅析中国古代宗法制度