镁铝尖晶石透明陶瓷的制备与光学性能研究
毕业论文关键词：镁铝尖晶石；生产制备；光学透过率。
Fabrication and optical properties of magnesia-alumina spine
Abstract：Because of the characteristics of transparent magnesia alumina magnesia-alumina spine ceramic material with ceramic: abrasion resistance,corrosion resistance,high temperature resistance,impact resistance,high strength,high hardness, good electrical insulation properties,but also the optical properties of sapphire single crystal and its close, the optical transmittance in the ultraviolet, visible light, infrared light is good, these features make the armor, in a transparent high intensity window and dome material application attention. In this paper some research results at home and abroad, introduces the optical transmitttance., transparent magnesia alumina magnesia-alumina spine ceramic production preparation and application development.
Key words: magnesia-alumina spine; preparation; optical transmittance.
目录
1.绪论 1
1.1引言 1
1.2镁铝尖晶石的结构 1
1.3镁铝尖晶石的性质 3
1.4影响陶瓷透光率的因素 4
1.5透明陶瓷的优势 5
1.6陶瓷的成型方法 6
1.6.1 干法成型 6
1.6.2 湿法成型 7
2.实验与表征 11
2.1实验原料 11
2.2 样品的制备 11
2.3 性能表征与测试方法 11
3．镁铝尖晶石（MgAl2O4）透明陶瓷光学性能的结果与分析 12
3.1 原料的表征 12
3.2 样品的XRD分析结果 13
3.3 透过率的测试与分析 14
3.4 吸收系数的测试与分析 15
3.5样品晶粒图的分析 16
3.6实验中存在的问题和结果分析 16
4.实验结论和主要创新点 16
4.1实验结论 16
4.2主要创新点 17
参考文献 18
致谢 20
1绪论
1.1引言
镁铝尖晶石能够在自然界自然形成，大多在火成岩和镁质灰岩或者是白云岩相接触的眼袋附近生成，这些区域都有一个共同的特点就是附近温度高，这是镁铝尖晶石生成的重要条件，并且伴生矿一般为辉石或者石榴石。但是由于形成条件的严苛和开采难度的问题，自然条件下形成的镁铝尖晶石能被利用的数量并不大，而且纯度也是一个问题，所以能否人为地制备镁铝尖晶石就成了一个重要课题，据1945年的研究报道，采用焰熔法可以成功的制备镁铝尖晶石单晶，这一技术的出现使得镁铝尖晶石被广泛运用得到实现，上世纪九十年代，玩过自主研制的镁铝尖晶石透明多晶体问世，由于这种新型透明陶瓷的机械性能和光学性能都与白宝石有相似之处，同时又具有低成本，抑郁制作成较大尺寸的器件等优点，成功地在军事和民用两方面得到推广。下面对镁铝尖晶石的结构和性质作简单的介绍。
1.2镁铝尖晶石的结构