摘要：上转换材料是一种重要的稀土发光材料，因其具有独特的发光特性，从而在多方面有着极为广泛的应用。本文重点介绍了目前具有最高上转换效率的材料体系，即以NaYF4为基质的上转换发光材料NaYF4:Yb,Er，归纳总结了其形貌和发光性质的研究进展。首先，当以不同的表面活性剂制备材料，即加入不同的表面活性剂时，所得的NaYF4:Yb,Er样品的形貌也将不同,但其发射光谱的发射峰位置基本相同，同时发现NaYF4:Yb,Er的发光强度跟颗粒大小、表面性质及结晶度有关；其次，用不同制备方法制备出的NaYF4:Yb,Er样品具有不同的形貌，且可获得两种晶相——立方相和六方相，并发现，在立方相时，NaYF4:Yb,Er荧光粉绿光的发射强度要高于红光的发射强度，而在六方相中，红光的荧光强度要相对高于绿光的强度。93959
毕业论文关键词：上转换材料，发光性质，NaYF4:Yb,Er
Abstract: As an important rare earth luminescent material, the upconversion material has found wide application in many fields owing to its significant advantages。 The paper presents the morphologies and luminescent properties of NaYF4-based phosphors, the upconversion material system with high conversion efficiency。 When the samples were prepared with different surfactants, the morphologies of the samples were different, but the emission peaks of emission spectrum were basically the same。 The luminous intensity of NaYF4:Yb3+,Er3+ is associated with particle size, surface properties and crystallinity。 The samples of NaYF4:Yb3+,Er3+ prepared by different methods only present two types of morphologies: cubic phase and hexagonal phase。 In the cubic phase, the green emission intensity emitted by the phosphor of NaYF4:Yb3+,Er3+ is higher than that of the red one。 In the hexagonal phase, the fluorescence intensity of red emission is higher than that of the green one。
Keywords: upconversion material, luminescence properties, NaYF4:Yb,Er
目录
1。绪论 3
1。1上转换发光材料简介 3
1。2 上转换材料的应用 3
1。2。1 生物检测 3
1。2。2上转换激光器 4
1。2。3红外防伪 4
1。3上转换材料的发光原理和结构 4
1。3。1 上转换材料的发光原理 4
1。3。2 稀土离子的电子层结构 5
1。4 上转换材料荧光纳米材料的制备方法 5
1。4。1 高温固相法 5
1。4。2 水热法 6
2。上转换材料 NaYF4:Yb3+,Er3+的形貌及发光性质的研究 6
2。1表面活性剂对NaYF4:Yb3+,Er3+的形貌和发光性质的研究 6
2。1。1 X射线粉末衍射图谱 6
2。1。2 SEM表征 7
2。1。3上转换发光光谱测定 7
2。2 不同的制备方法对的NaYF4:Yb3+,Er3+形貌和发光性质的影响 8
2。2。1 水热法制备NaYF4:Yb3+,Er3+ 8
2。2。2 固相法制备NaYF4:Yb3+,Er3+的影响 12
2。2。3 共沉淀法制备NaYF4:Yb3+,Er3+的影响 14
2。2。4 核-壳包覆对NaYF4:Yb3+,Er3+的影响 上转换材料NaYF4:Yb,Er的形貌及发光性质研究进展:http://www.youerw.com/wuli/lunwen_201903.html