负载型纳米金催化剂载体的制备

时间:2020-04-07 09:12来源:毕业论文
以聚硅氧烷为一种聚合物与N-异丙基丙烯酰胺、4-乙烯基吡啶、乙酸乙烯酯等形成半互穿聚合物网络来作为纳米金催化剂的载体

摘要纳米金催化剂对许多反应具有催化作用,且具有很高的催化活性,因此引发了广大化学学者的关注。金的催化化学已迅速成为一个几乎每个星期都有新发现的热门课题。两种高分子材料聚合物分子链相互交联以化学键的形式形成半互穿聚合物网络结构。半互穿聚合物网络结构具有较好的性能,结构稳定,可以作为金属催化剂的载体。本文以聚硅氧烷为一种聚合物与N-异丙基丙烯酰胺、4-乙烯基吡啶、乙酸乙烯酯等形成半互穿聚合物网络来作为纳米金催化剂的载体。47588

Nano-gold catalyst has catalytic activity for many reaction , and has high catalytic activity, thus triggering the concern of the majority of chemical scholars. The catalytic chemistry of gold has rapidly become a hot topical which has a new found every week . Two kinds of polymer materials cross-linked polymer chains in the form of a chemical bond to form a semi-interpenetrating polymer network structure. Semi-interpenetrating polymer network structure has better performance, structural stability, can be used as a carrier of metal catalyst. In this paper, the polysiloxane is a polymer with N- isopropyl acrylamide formation of 4-vinyl pyridine, vinyl acetate, and other semi-interpenetrating polymer network as the carrier of nano-gold catalyst .

毕业论文关键词:纳米金催化剂; 载体; 聚硅氧烷

Keyword: Nano-gold catalyst;Carrier ;Polysiloxane 

目    录

1. 引言 6

2. 实验部分 6

2.1 本实验研究背景及内容 6

2.1.1研究背景 6

2.1.2研究内容 7

2.2 实验药品及仪器设备 7

2.3 实验方法 8

2.3.1样品一制备过程 8

2.3.2样品二制备过程 8

2.3.3样品三制备过程 8

2.3.4样品四制备过程 9

2.3.5样品五制备过程 9

2.3.6样品六制备过程 9

2.3.7样品七制备过程 9

2.4 样品数据表征 10

2.4.1傅里叶红外光谱分析 10

2.4.2 差式扫描量热分析(DSC) 16

2.4.3 热重分析(TG) 21

3. 结论与展望 28

参考文献 29

致谢 30 

表索引

表 2 1实验药品及其产地 7

表 2 2主要仪器及生产地 8

 图索引

图 2 1样品一的傅里叶红外光谱图 9

图 2 2样品二的傅里叶红外光谱图 10

图 2 3样品三的傅里叶红外光谱图 11

图 2 4 样品四的傅里叶红外光谱图 12

图 2 5 样品五的傅里叶红外光谱图 13

图 2 6 样品六的傅里叶红外光谱图 14

图 2 7 样品七的傅里叶红外光谱图 15

图 2 8 样品一的差式扫描量热分析图 负载型纳米金催化剂载体的制备:http://www.youerw.com/yixue/lunwen_49745.html

------分隔线----------------------------
推荐内容