摘要本文对半径为6.5mm的B7钢试样在淬火温度为830～890℃、保温时间为60～120min内，采用不同温度的水和不同浓度的盐水作为冷却介质，进行了上述不同热处理工艺条件下的淬硬性实验研究。半径为6.5mm的B7钢试样在淬火温度为860℃，保温时间为60min时，采用盐水冷却能获得更高的淬硬性强度。当盐水温度相同时，盐水的浓度越高，冷却能力越好，获得B7钢的淬硬性强度越高。22638
毕业论文关键词：B7钢；冷却介质；淬硬性强度
Abstract
The thesis is about B7 steel samples  of 6.5mm radius in quenching temperature 830 ～ 890 ℃, holding time 60 ~ 120min, using water of different temperature and salt water of different potency as the cooling medium for the hardenability test research of different heat treatment conditions. when the quenching temperature is 860 ℃, the holding time is 60min and salt water is chosen as the cooling medium, the B7 steel samples of 6.5mm radius will get higher hardenability strength. when the salt water temperature is equal, the higher potency the salt water is, the better the cooling ability wil be, then the better hardenability strength the B7 steel will get.
KeyWords：B7 steel；cooling medium；hardenability strength
目录
1    文献综述    1
1.1 课题研究的目的和意义    1
1.2    B7钢简介    1
1.2.1    B7钢的成分    1
1.2.2    B7钢的工艺    1
1.2.3    B7钢的性能    2
1.2.4    B7钢的应用    2
1.3    淬硬性概述    2
1.3.1    淬硬性的机理    2
1.3.2 淬硬性的影响因素    3
1.3.2    淬硬性的测定方法    3
1.3.3    淬硬性指标的应用    4
1.3.4    实现淬硬性指标的影晌因素    4
1.4    国内外相关研究    5
1.4.1    国外论文的研究    5
1.4.2    国内论文的研究    5
1.5    相近钢种42CrMo的研究    5
1.5.1    42CrMo简介    5
1.5.2    冷却条件对42CrMo的影响    6
2    实验部分    7
2.1    实验内容    7
2.2    实验方法    7
2.2.1    主要方法    7
2.2.2    分析方法    7
2.3    实验方案    8
2.3.1    方案设计    8
2.3.2    方案说明    8
2.4    实验器材与设备    8
2.4.1    器材    8
2.4.2    设备    9
2.5    实验步骤    9
2.5.1    实验具体工作    9
2.5.2    实验进度安排    11
3    结果与分析    12
3.1    原始试样测定结果    12
3.2    第一轮实验结果    12
3.2.1    数据分析    13
3.2.2    定量分析    13
3.2.3    小结    13
3.3    第二轮实验结果    13
3.3.1    定量分析    14 B7钢的淬硬性影响研究+文献综述:http://www.youerw.com/cailiao/lunwen_15338.html