摘要本文以316L不锈钢为原料，利用旋转加速喷丸（Rotational Accelerated Shot Peening, RASP）设备在样品上进行表面纳米化处理，对其进行其微观组织的观察，粗糙度的测试。得到以下结论：
1.316L不锈钢经过喷丸处理，表面向内部晶体的塑性变形越来越小，最表层变形最严重，晶粒尺寸呈梯度分布。随着处理时间的增加，塑性变形带来的影响范围更大，厚度方向上晶粒的尺寸变化范围也越大，最表层的晶粒也相对较细。
2. 相同厚度的316L不锈钢经过不同时间的表面纳米化处理时，样品的线粗糙度和面粗糙度随着处理时间的增加而增加，22958
3. 透射电镜结果表明，RASP处理成功在316L不锈钢表面引入纳米层。表面变形孪晶片层平均在23nm，纳米晶粒平均短轴尺寸在30nm左右。
关键词 表面纳米化处理 316L不锈钢 微观结构 粗糙度
毕业设计说明书（毕业论文）外文摘要
Title Microstructures research of 316L stainless steel induced by surface nanocrystallization
Abstract
In the present work, by means of Rotational Accelerated Shot Peening (RASP), 316L stainless steel was chosen as raw material and was surface treated. Microstructures and surface roughness were characterized, and the main conclusions included:
1. After RASP treatment, the cross-sectional of the 316L stainless steel shows a gradient structures, the microstructures were quite different because of the different deformation strain along the cross section, from surface to the interior.
2. The surface line roughness and face roughness were both increased with the increase of the RASP treatment time.
3. TEM results showed that the RASP treatment could successfully introduce nano-layer to the 316L stainless steel. The average twin/matrix lamellar thickness in top surface is 23nm while the average short-axis grain size is 30nm.
Keywords Surface nanocrystallization microstructures roughness
目 次
1 绪论 1
1.1 纳米材料的简介 1
1.2 纳米材料的制备 1
1.3 表面纳米化的基本方式、制备方法和技术优势 1
1.3.1 表面纳米化的基本方式 1
1.3.2 塑性变形致金属材料表面纳米化 2
1.3.3 金属材料表面纳米化技术优势 4
1.4 316L不锈钢表面纳米化 5
1.5 316L不锈钢表面纳米化的研究现状 5
1.6 316L不锈钢表面纳米化的影响因素 6
1.6.1 微观形貌 6
1.6.2 残余应力 6
1.6.3 组织结构 6
1.7 本文研究的内容 7
2 实验部分 8
2.1 实验材料 8
2.2 试样制备过程 8
2.3 性能测试与表征 9
2.3.1 金相观察 9
2.3.2 粗糙度测试 10
2.3.3 透射电镜观察 10
3 实验结果与讨论 12
3.1 金相观察分析 12
3.2 粗糙度测试分析 13
3.3 透射电镜观察分析 19
结 论 21
致 谢 22
参考文献23
1 绪论
1.1 纳米材料的简介
广义地说，纳米材料是指三文空间中至少有一文处在纳米尺度范围（0.1nm～100nm）或由他们作为基本单元构成的材料[1]。如果按文数,纳米材料的基本单元可分为三类： 316L不锈钢表面纳米化处理结构观察:http://www.youerw.com/cailiao/lunwen_15834.html