摘要：本实验是以三聚氰胺与甲醛溶液为原料，用氢氧化钠溶液调节其PH值为9，在35℃的条件下发生羟甲基反应生成预聚体；以盐酸调节体系的PH至为5，预聚物在在该条件下分散在石油醚中进行反向悬浮聚合，生成三聚氰胺甲醛树脂微粒。并对微粒进行红外光谱分析，结果表明生成的微粒为三聚氰胺甲醛树脂。这对提高三聚氰胺甲醛树脂的使用性是很有意义的。5895
关键词：    离子交换，三聚氰胺，缩合反应，反向聚合，悬浮聚合，珠状
The Study of Methods for Prepare Melamine Resin
Abstract:  The experiment is based on melamine and formaldehyde solution as raw material
and use Sodium hydroxide solution to adjust its PH value of 9. Then under the conditions at 35 ℃ which makes hydroxymethyl prepolymer reaction happen.Use Hydrochloric acid to adjust the PH of 5. In that condition prepolymer dispersed in petroleum ether, reverse suspension polymerization which generates Melamine-formaldehyde resin particles. IR spectrum of the fine particles shows that the generated particles are melamine formaldehyde resin which is meaningful to improve of the use of melamine-formaldehyde resin.
Key Words:    Ion exchange；Melamine；Condensation reaction；Reverse polymerization；Suspension Polymerization；Beaded
目录
摘要    i
Abstract    i
目录    ii
1    绪论    1
1.1    离子交换树脂的基本介绍    1
1.2    离子交换树脂的工作原理    1
1.2.1    晶格理论    2
1.2.2    双电层理论    3
1.2.3    Donnan膜理论    3
1.3    离子交换高分子树脂的制备    3
1.3.1    加成聚合    4
1.3.2    缩聚反应制备树脂    4
1.4    离子交换树脂的应用    5
1.5    本课题研究目的和内容    5
1.5.1    三聚氰胺与甲醛的摩尔比的影响    6
1.5.2    反应介质的pH 值的影响    6
1.5.3    反应温度的影响    6
2    试验部分    7
2.1    药品    7
2.2    仪器和设备    8
2.3    实验步骤    8
2.3.1    三聚氰胺树脂制备中原料配比的确定及计算    8
2.3.2    制取三聚氰胺预聚物即羟甲基三聚氰胺    9
2.3.3    聚甲基丙烯酸甲脂（PMMA）的制备    10
2.3.4    反向悬浮聚合阶段    11
2.4    性能测试：红外测试    12
3    结果与讨论    13
3.1    制取三聚氰胺预聚物的反应    13
3.1.1    实验现象及过程分析    13
3.1.2    反应过程及产物的分析    14
3.2    制取聚甲基丙烯酸甲脂（PMMA）的反应    14
3.2.1    实验现象分析    14
3.2.2    反应过程及产物的分析    14
3.3    羟甲基三聚氰胺的反向悬浮聚合反应    15
3.3.1    实验现象及过程分析    15
3.3.2    红外谱图分析    17 三聚氰胺树脂的制备方法研究+文献综述:http://www.youerw.com/cailiao/lunwen_3165.html