摘要：本论文开始主要阐述了等径角挤压、往复挤压、高压扭转和累积叠轧等强烈变形的方法和特点，它们通过增大变形量来改变晶粒的大小，并对产品的组织性能进行分析。由此引出反复弯曲的概念，并通过实验的方法验证其对铜合金组织（晶粒）的变化规律。进一步分析此组合变形铜合金（低层错能）性能影响。最后与使用用同种变形方法的铝合金（高层错能）进行对比。6099
关键词： 强烈变形；晶粒细化；层错能；铜合金；反复弯曲
After Rolling Bent Copper Alloy
Microstructure and Properties of its
Abstract: Beginning of this article mainly elaborated ECAP, reciprocating extrusion, high pressure torsion and accumulative roll method and other strong deformation characteristics, they are changed by increasing the amount of deformation of the grain size, and analyzes the performance of the product organization. This leads to the concept of repeated bending and verified through experimental methods for copper alloy ( grain ) were studied. Further analysis of this combination deformed copper alloys ( low stacking fault energy ) performance impact. Finally with the use of the method with the same kind of deformed aluminum ( high stacking fault energy ) were compared.
Key Words:  Strongly deformed; grain refinement; stacking fault energy; copper alloy; repeated bending
目 录
1    文献综述    4
1.1    等径角挤压    4
1.2    往复挤压    2
1.3    高压扭转    4
1.4    累积叠轧    4
1.5    强度行为    5
1.6    超塑性    6
1.7    应变诱导晶粒细化的机制    6
1.8    组织演化    7
1.8.1    中、低层错能纯铜材料在ECAP中的组织演化    7
1.8.2    高层错能45钢中铁素体在ECAP中的组织演化    8
1.8.3    高层错能45钢中珠光体在ECAP中的组织演化    9
2    研究内容和目标    10
2.1    研究内容    10
2.2    研究目标    10
3    研究材料介绍    11
3.1    化学成分    11
3.2    力学性能    11
3.3    热处理规范    11
4    实验仪器    12
4.1    箱式电阻炉    12
4.2    Φ350MM多功能二辊实验轧机    13
4.3    电液伺服万能试验机    14
4.4    金相镶嵌机    15
4.5    金相试样抛光机    16
4.6    MDJ—DM显微镜    17
5    实验步骤    18
5.1    轧制    18
5.2    弯曲试验    18
5.3    取样镶嵌    20
5.4    抛光腐蚀    21
6    实验结果    22
6.1    随压下量变化铜合金的组织变化规律    22
6.2    经反复弯曲后铜合金的组织变化规律    26
7    总结    29
7.1    分析与讨论    29
7.1.1    弯曲变形量的计算    29 铜合金轧后弯曲变形对其组织与性能的影响:http://www.youerw.com/cailiao/lunwen_3455.html